Low-temperature diesel oxidation catalysts using TiO2 nanowire arrays integrated on a monolithic substrate
Metal oxide nanoarrays, such as titanium oxide nanoarrays, having a platinum group metal dispersed thereon and methods of making such nanoarrays are described. The platinum group metal can be dispersed on the metal oxide nanoarray as single atoms. The nanoarrays can be used to catalyze oxidation of combustion exhaust.
1. A method of making a titanium dioxide nanoarray having a platinum group metal dispersed thereon, the method comprising:
contacting a substrate with a Ti (IV) precursor in a non-polar solvent and with hydrochloric acid in water under hydrothermal conditions, thereby forming a titanium dioxide nanoarray
contacting the titanium dioxide nanoarray with a solution comprising a platinum group metal precursor;
drying the titanium dioxide nanoarray; and
calcining the titanium dioxide nanoarray;
wherein the titanium dioxide nanoarray is mesoporous.
2. The method of claim 1 , wherein the platinum group metal precursor is a platinum precursor.
3. The method of claim 2 , wherein the platinum precursor is Pt(NH 3 ) 4 (NO 3 ) 2 .
4. The method of claim 1 , where the solution comprising a platinum group metal precursor further comprises sodium ions.
5. The method of claim 4 , wherein the sodium ions are from sodium hydroxide (NaOH).
6. The method of claim 1 , wherein drying the titanium dioxide nanoarray comprises microwaving the titanium dioxide nanoarray.
7. The method of claim 1 , further comprising contacting the titanium dioxide nanoarray with a solution having a platinum precursor dissolved therein and drying the titanium dioxide nanorarray at least twice prior to calcining the titanium dioxide nanoarray.
8. The method of claim 1 , wherein calcining is performed at a temperature between about 450° C. and 550° C. for a duration from 3 hours to 4 hours.
9. The method of claim 1 , wherein calcining is performed with a ramp rate of 2° C./min.
10. The method of claim 1 , wherein a water:non-polar solvent ratio is from about 1:20 to about 1:5.
11. The method of claim 10 , wherein the non-polar solvent comprises one or more of butanone, toluene, and hexane.
12. The method of claim 11 , wherein the hexane is n-hexane.
13. The method of claim 1 , wherein the titanium (IV) precursor comprises one or more titanium alkoxides.
14. The method of claim 13 , wherein the titanium (IV) alkloxide is titanium (IV) isopropoxide or titanium (IV) n-butoxide.
15. The method of claim 1 , wherein the titanium (IV) precursor comprises titanium tetrachloride.
16. The method of claim 1 , wherein the substrate is seeded with TiO 2 prior to reacting the substrate.
17. The method of claim 1 , wherein the hydrochloric acid solution is from 25 wt % to 45 wt % hydrochloric acid.
18. An article comprising:
a substrate;
a mesoporous, rutile titanium dioxide nanoarray integrated onto the substrate;
a platinum group metal disposed on the titanium dioxide nanoarray.
19. A method of oxidizing a combustion exhaust, the method comprising:
contacting a source of combustion exhaust with a mesoporous, rutile titanium dioxide nanoarray having a platinum group metal dispersed thereon.