Hot-dip galvanized steel material having excellent weldability and press workability and manufacturing method therefor
Provided are a hot-dipped galvanized steel material and a method for manufacturing the same. The hot-dipped galvanized steel material comprises an iron substrate and a hot-dipped galvanizing layer formed on the iron substrate, wherein the hot-dipped galvanizing layer comprises, by wt %, 0.01 to 0.5% of Al, 0.01 to 1.5% of Mg, 0.05 to 1.5% of Mn, 0.1 to 6% of Fe, and the balance of Zn and inevitable impurities, with a Zn—Fe—Mn based alloy phase present at the interface between the iron substrate and the hot-dipped galvanizing layer, and an area ratio of the Zn—Fe—Mn-based alloy phase to the hot-dipped galvanizing layer ranging from 1 to 60%.
1. A hot-dip galvanized steel material comprising:
base steel and a hot-dip galvanized layer disposed on the base steel,
wherein the hot-dip galvanized layer comprise, by wt %, 0.01 to 0.5% of Al, 0.01 to 1.5% of Mg, 0.05 to 1.5% of Mn, 0.1 to 6% of Fe, and a balance of Zn and inevitable impurities, and
a Zn—Fe—Mn based alloy phase is present at an interface between the base steel and the hot-dip galvanized layer, and
a ratio of an area of the Zn—Fe—Mn based alloy phase to an area of the hot-dip galvanized layer is 1% to 60%.
2. The hot-dip galvanized steel material of claim 1 , wherein the Zn—Fe—Mn based alloy phase is (Fe,Mn)Zn 7 .
3. The hot-dip galvanized steel material of claim 1 , wherein the base steel comprises P in an amount less than 0.01%.
4. The hot-dip galvanized steel material of claim 1 , wherein the hot-dip galvanized layer further comprises 0.0001 to 1 wt % in total of one or more selected from a group consisting of K, Ca, and Li.
5. The hot-dip galvanized steel material of claim 1 , wherein one-side coating amount of the hot-dip galvanized layer is 10 to 200 g/m 2 .