Composition with thermal conductivity and laser plating performance by core-shell structure LDS additive with metal compounds coated on mineral filler surface
The disclosure concerns thermally conductive polymer compositions comprising: (a) from about 20 wt % to about 80 wt % of at least one polymer component; (b) from greater than about 0 wt % to about 70 wt % of a thermally conductive filler; and (c) from about 0.1 wt % to about 40 wt % of a laser activatable additive having a core-shell structure; wherein the core comprises an inorganic filler and the shell comprises a laser activatable component; wherein the combined weight percent value of all components does not exceed about 100 wt %; wherein all weight percent values are based on the total weight of the composition; and wherein a molded sample of the blended thermoplastic composition has a through plane thermal conductivity of at least about 0.40 W/m·K when determined in accordance with ASTM E1461.
1. A thermally conductive polymer composition comprising:
a. from about 20 wt % to about 80 wt % of at least one polymer component, wherein the polymer component comprises a polycarbonate;
b. from greater than about 0 wt % to about 70 wt % of a thermally conductive filler; and
c. from about 0.1 wt % to about 40 wt % of a laser activatable additive having a core-shell structure; wherein the core comprises an inorganic filler and the shell comprises a laser activatable component,
wherein the combined weight percent value of all components does not exceed 100 wt %,
wherein all weight percent values are based on the total weight of the composition,
wherein a molded sample of the composition has a through plane thermal conductivity of at least about 0.40 W/m·K when determined in accordance with ASTM E1461, and wherein a molded sample of the composition exhibits a notched Izod impact strength of at least 66 J/m when tested in accordance with ASTM D256 at 23° C.
2. The composition of claim 1 , wherein the thermally conductive filler comprises: a high thermally conductive filler having a thermal conductivity greater than or equal to about 50 W/m·K; or a low thermally conductive filler having a thermal conductivity from about 10 W/m·K to about 30 W/m·K; or a combination thereof.
3. The composition of claim 2 , wherein the high thermally conductive filler is selected from the group consisting of aluminum nitride AlN, aluminum carbide Al 4 C 3 , aluminum oxide Al 2 O 3 , boron nitride BN, aluminum oxynitrides AlON, magnesium silicon nitride MgSiN 2 , silicon carbide SiC, silicon nitride Si 3 N 4 , graphite, expanded graphite, graphene, carbon fiber, and combinations thereof.
4. The composition of claim 2 , wherein the low thermally conductive filler is selected from the group consisting of Mg(OH) 2 (Magnesium hydroxide), steatite H 2 Mg 3 (SiO 3 ) 4 (Talc), γ-AlO(OH) (boehmite),α-AlO(OH) (diaspore), Al(OH) 3 (gibbsite), CaCO 3 , mica, barium oxide BaO, barium sulfate BaSO 4 , wollastonite CaSiO 3 , zirconium oxide ZrO 2 , silicon oxide SiO 2 , glass beads, magnesium aluminate MgO.xAl 2 O 3 , dolomite CaMg(CO 3 ) 2 , ceramic-coated graphite, clay, and combinations thereof.
5. The composition of claim 1 , wherein the shell is a metal, metal oxide, or mixed-metal oxide.
6. The composition of claim 1 , wherein the core is a metal oxide, mica, talc, aluminum nitride AlN, Al 4 C 3 , BN, MgSiN 2 , SiC, Si 3 N 4 , graphite, expanded graphite, graphene, carbon fiber, ZnS, glass beads, clay, or a combination thereof.
7. The composition of claim 1 , wherein the shell component has a thickness of from about 1 nm to about 50 μm.
8. The composition of claim 1 , wherein the core has a mean particle size of about 50 nm to about 500 μm.
9. The composition of claim 1 , wherein the core component is about 2% to about 70% by weight, with the balance of the laser activatable additive being the shell.
10. The composition of claim 1 , further comprising glass fiber.
11. The composition of claim 1 , further comprising an organic or inorganic flame retardant.
12. The composition of claim 1 , the polymer component further comprising a chemical reactive or non-chemical reactive impact modifier.
13. The composition of claim 1 , further comprising an additive comprising an antioxidant, a lubricant, a thermal stabilizer, an ultraviolet light absorbing additive, a plasticizer, an anti-dripping agent, a mold release agent, an antistatic agent, a dye, a pigment, or a radiation stabilizer, or a combination thereof.
14. The composition of claim 1 , wherein a molded sample of the composition exhibits a plating index value of at least about 0.6.
15. An article comprising a composition of claim 1 .
16. The article of claim 15 , wherein the article is selected from a computer device, electromagnetic interference device, printed circuit, global positioning system device, cellular antenna device, smart phone device, automotive device, medical device, sensor device, security device, shielding device, shadowless lamp, radiofrequency antenna device, light emitting diode device and radio frequency identification device.
17. A method of manufacturing an article comprising:
a. molding an article from the composition of claim 1 ;
b. exposing the laser activatable additive to a laser to form an activated area; and
c. plating a metal layer onto the activated area.
18. The thermally conductive polymer composition of claim 1 , comprising:
a. from about 50 wt % to about 70 wt % of the polymer component;
b. from about 10 wt % to about 20 wt % of the thermally conductive filler; and
c. from about 2 wt % to about 10 wt % of the laser activatable additive.
19. The composition of claim 1 , wherein the core is mica, talc, aluminum nitride AlN, Al 4 C 3 , Al 2 O 3 , BN, AlON, MgSiN 2 , SiC, Si 3 N 4 , graphite, expanded graphite, graphene, carbon fiber, ZnS, CaO, MgO, ZnO, TiO 2 , Mg(OH) 2 ,γ-AlO(OH) (boehmite), α-AlO(OH) (diaspore), Al(OH) 3 (gibbsite), CaCO 3 , BaO, BaSO 4 , CaSiO 3 , ZrO 2 , SiO 2 , glass beads, MgO.xAl 2 O 3 , CaMg(CO 3 ) 2 , clay, or a combination thereof.