Double diaphragm shaping of composite materials, assemblies for such shaping, and resulting composite materials
Disclosed herein are methods for isolating a composite material from the environment, as well as the isolated composite material. Also disclosed herein are methods for shaping a composite material that include the use of isolated composite materials. For example, disclosed is a method for mechanical thermoforming of a composite material to form a shaped composite material.
1. A method for shaping a composite material, the method comprising:
(a) placing a substantially planar composite material between an upper flexible diaphragm and a lower flexible diaphragm by creating a sealed pocket between the diaphragms which houses the composite material,
(b) bringing the upper flexible diaphragm and the lower flexible diaphragm into intimate contact with the composite material, thereby forming a layered structure, wherein the composite material is held stationary between the upper flexible diaphragm and the lower flexible diaphragm until heat or force is applied to the layered structure;
(c) optionally pre-heating the layered structure in a heating apparatus at a temperature sufficient to either lower the viscosity of the composite material or soften the diaphragms;
(d) positioning the layered structure in a press tool comprising a male mold and a corresponding female mold separated by a gap, wherein the male mold and the female mold each independently have a non-planar molding surface,
(e) compressing the layered structure between the male mold and the female mold by closing the gap between the male mold and the female mold; and
(f) maintaining the male mold and the female mold in a closed position until the viscosity of the layered structure reaches a level sufficient to maintain a molded shape.
2. The method of claim 1 , wherein step (e) comprises partially closing the gap between the male mold and the female mold such that a smaller gap is formed between the molds, which smaller gap is subsequently closed after a specific time or viscosity is reached.
3. The method of claim 1 , wherein the male mold and the female mold are maintained at a temperature above ambient temperature.
4. The method of claim 1 , wherein step (e) comprises closing the gap between the male mold and the female mold at a speed of between about 0.7 mm/s and about 400 mm/s, while maintaining the male mold and the female mold at a temperature above the softening point of the composite material.
5. The method of claim 1 , further comprising (g) cooling the layered structure on the tool to a temperature that is below the softening temperature of the composite material or (g′) removing the layered structure from the tool while the layered structure is above the softening temperature of the composite material.
6. The method of claim 1 , further comprising machining the composite material according to a pattern prior to step (a).
7. The method of claim 1 , wherein the upper diaphragm and the lower diaphragm are each independently selected from a film comprising one or more layers, each independently selected from a rubber layer, a silicone layer and a plastic layer.
8. The method of claim 1 , wherein the layered structure is positioned in the press tool and in the optional heating apparatus by automated means.
9. The method of claim 1 , wherein no vacuum pressure is applied to any portion of the press tool.
10. The method of claim 1 , wherein the composite material comprises structural fibers of a material selected from aramid, high-modulus polyethylene (PE), polyester, poly-p-phenylene-benzobisoxazole (PBO), carbon, glass, quartz, alumina, zirconia, silicon carbide, basalt, natural fibers and combinations thereof.
11. The method of claim 1 , wherein the composite material comprises a binder or matrix material selected from thermoplastic polymers, thermoset resins, and combinations thereof.