Positive electrode active material for nonaqueous electrolyte secondary batteries, and nonaqueous electrolyte secondary battery
A positive electrode active material for nonaqueous electrolyte secondary batteries includes secondary particles of lithium transition metal oxide including aggregates of primary particles of the oxide. The primary particles have an average particle size of not less than 1 μm, and the secondary particles have a void content of more than 30%.
1. A positive electrode active material for nonaqueous electrolyte secondary batteries, comprising secondary particles of lithium transition metal oxide comprising aggregates of primary particles of the oxide,
the primary particles having an average particle size of not less than 1 μm, the secondary particles having a void content of more than 30%,
wherein the positive electrode active material includes a long void that is continuous from a surface of the secondary particle over a length of more than ⅙ of a particle diameter, and a proportion of the long voids relative to voids within the secondary particles is not less than 50%.
2. The positive electrode active material for nonaqueous electrolyte secondary batteries according to claim 1 , wherein the pore size diameter distribution of the secondary particles has a peak in the range of 0.3 to 1.0 μm on a distribution curve.
3. The positive electrode active material for nonaqueous electrolyte secondary batteries according to claim 1 , wherein the compressive fracture strength of the secondary particles is in the range of 200 to 500 MPa.
4. The positive electrode active material for nonaqueous electrolyte secondary batteries according to claim 1 , wherein the crystallite size of the lithium transition metal oxide is not less than 200 nm and the crystal distortion of the lithium transition metal oxide is less than 0.2%.
5. A nonaqueous electrolyte secondary battery comprising a positive electrode, a negative electrode and a nonaqueous electrolyte,
the positive electrode comprising the positive electrode active material for nonaqueous electrolyte secondary batteries described in claim 1 .
6. The positive electrode active material for nonaqueous electrolyte secondary batteries according to claim 1 , wherein a ratio of longer diameter to shorter diameter (longer diameter/shorter diameter) of 50% or more of the primary particles forming the secondary particles is 2 or more.