Mineral wool
Mineral wool fibers having a mineral wool fiber composition are manufactured by introducing batch materials into a melter, melting the mineral batch materials in the melter to provide a melt and fiberizing the melt to form the mineral wool fibers. The batch materials comprise i) fibers having a first batch material composition which is different from the mineral wool fiber composition and consisting of scrap fibers which have broken at a bushing producing continuous fibers; and ii) one of more additional mineral batch materials.
1. A method of manufacturing mineral wool fibers having a mineral wool fiber composition, wherein the mineral wool fiber composition comprises:
30 to 55 wt % SiO 2 , and
10 to 30 wt % Al 2 O 3 , and
4 to 14 wt % total iron expressed as Fe 2 O 3 , and
a combination selected from:
a) 20 to 35 wt % of the combination of CaO and MgO; and less than 8 wt % of the combination of Na 2 O and K 2 O; and
b) 8 to 23 wt % of the combination of CaO and MgO; and 4 to 24 wt % of the combination of Na 2 O and K 2 O;
the method comprising:
providing a first batch material in the form of fibers having a first batch material composition, the fibers of the first batch material consisting of scrap fibers which have broken at a bushing producing continuous fibers, the first batch material composition being different from the mineral wool fiber composition, and the first batch material composition comprising:
52 to 62 wt % SiO 2 , and
12 to 16 wt % Al 2 O 3 , and
16 to 25 wt % CaO, and
0 to 5 wt % MgO, and
0 to 10 wt % B 2 O 3 , and
0 to 2 wt % of the combination of Li 2 O+Na 2 O+K 2 O, and
0 to 1.5 wt % TiO 2 , and
0.005 to 1 wt % total iron expressed as Fe 2 O 3 , and
0 to 1 wt % fluoride;
providing one of more additional mineral batch materials;
introducing the mineral batch materials into a melter, melting the mineral batch materials in the melter to provide a melt and fiberizing the melt to form the mineral wool fibers that have the mineral wool fiber composition.
2. The method of claim 1 , wherein the fibers of the first batch material comprise an organic coating present in a quantity of at least 2 wt % with respect to the total weight of the first batch material.
3. The method of claim 1 , wherein the first batch material constitutes at least 10 to 60 wt % of the mineral batch materials.
4. The method of claim 1 , wherein the introducing the mineral batch materials into a melter comprises introducing the mineral batch materials into a melter selected from a submerged combustion melter, an electric arc furnace and a circulating furnace.
5. The method of claim 1 wherein the moisture content of the first batch material when introduced in to the melter is at least 10 wt %.
6. The method of claim 1 , wherein the one of more additional mineral batch materials comprise at least one material selected from: dolomite, calcined bauxite, steel slag and combinations thereof.
7. The method of claim 1 , wherein the one of more additional mineral batch materials comprise recycled portions of mineral wool insulation product from previous production of the mineral wool fibers.
8. The method of claim 1 , wherein the introducing the mineral batch materials into a melter comprises introducing the mineral batch into a cupola furnace.
9. The method of claim 1 , wherein first batch material composition comprises.
53 to 56 wt % SiO 2 , and
12 to 16 wt % Al 2 O 3 , and
20 to 24 wt % CaO, and
0 to 2 wt % MgO, and
4 to 8 wt % B 2 O 3 and
0.5 to 1.8 wt % of the combination of Li 2 O+Na 2 O+K 2 O, and
0 to 0.5 wt % TiO 2 , and
0.005 to 0.75 wt % total iron expressed as Fe 2 O 3 .
10. The method of claim 1 , wherein first batch material composition comprises.
55 to 57 wt % SiO 2 , and
12 to 15 wt % Al 2 O 3 , and
23 to 26 wt % CaO, and
1 to 4.5 wt % MgO, and
0.01 to 2.5 wt % B 2 O 3 and
0.5 to 1.8 wt % of the combination of Li 2 O+Na 2 O +K 2 O, and
0.01 to 1.5 wt % TiO 2 , and
0.005 to 0.75 wt % total iron expressed as Fe 2 O 3 .
11. A method of manufacturing mineral wool fibers having a mineral wool fiber composition, the method comprising:
providing a first batch material in the form of fibers having a first batch material composition, the fibers of the first batch material consisting of scrap fibers which have broken at a bushing producing continuous fibers, the first batch material composition being different from the mineral wool fiber composition, and the first batch material composition comprising:
52 to 62 wt % SiO 2 , and
12 to 16 wt % Al 2 O 3 , and
16 to 25 wt % CaO, and
0 to 5 wt % MgO, and
0 to 10 wt % B 2 O 3 , and
0 to 2 wt % of the combination of Li 2 O+Na 2 O+K 2 O, and
0 to 1.5 wt % TiO 2 , and
0.005 to 1 wt % total iron expressed as Fe 2 O 3 , and
0 to 1 wt % fluoride;
providing one of more additional mineral batch materials;
introducing the mineral batch materials into a submerged combustion melter, wherein the first batch material constitutes at least 10 wt % of the mineral batch materials, wherein the moisture content of the first batch material when introduced into the submerged combustion melter is at least 10 wt %, wherein the first batch material is introduced into the submerged combustion melter in the form of loose fibers, and wherein the one of more additional mineral batch materials comprise at least one material selected from: dolomite, calcined bauxite, steel slag, recycled portions of the mineral wool insulation product from previous production of the mineral wool fibers and combinations thereof;
melting the mineral batch materials in the submerged combustion melter to provide a melt and fiberizing the melt to form the mineral wool fibers have the mineral wool fiber composition;
wherein the mineral wool fiber composition comprises
30 to 55 wt % SiO 2 , and
10 to 30 wt % Al 2 O 3 , and
4 to 14 wt % total iron expressed as Fe 2 O 3 , and
a combination selected from:
a) 20 to 35 wt % of the combination of CaO and MgO; and less than 8 wt % of the combination of Na 2 O and K 2 O; and
b) 8 to 23 wt % of the combination of CaO and MgO; and 4 to 24 wt % of the combination of Na 2 O and K 2 O.