Arc flash resistant multilayered material having low thickness
A multi-layered material with low thickness is provided, having properties of thermal and electric insulation, flame retardant capacity and high mechanical strength, useful for the manufacture of personal protective equipment and more in general of work items for the protection against arc flash effects. The material provides a high grade of protection against arc flash with good flexibility and comfort for the wearer, who is thus protected without being hindered in movements.
1. A protective multi-layered material against arc flash, consisting of:
a fabric layer of para-aramid fibres (A), surmounted by a fabric layer of polyester flame-retardant fibres (B), and
a layer of silicone rubber (C2) incorporating therein micro-powder of iron (III) oxide, said layer (C2) being disposed on a side of said fabric layer (B) opposite from said fabric layer (A),
a further layer of silicone rubber (C1), intermediate said two layers of fibrous fabrics (A) and (B), and incorporating therein glass hollow microspheres and micro-powder of iron (III) oxide incorporated in said further layer of silicone rubber (C1),
said multi-layered material having a thickness lower than 1 mm,
wherein said glass hollow microspheres are incorporated in said layer (C1) in amount comprised of about 6% by weight with respect to the total weight of the layer wherein they are incorporated,
wherein said iron (III) oxide micro-powder is incorporated in said layer (C1) and in said layer (C2) in an amount comprised of about 5% by weight with respect to the total weight of the layers wherein they are incorporated,
wherein said glass hollow microspheres have a diameter size lower than 150 μm, and
wherein said iron (III) oxide particles in both layers of silicone rubber (C2 and C1) have average diameter size lower than 5 mm.
2. The multi-layered material according to claim 1 , having a thickness comprised between 0.60 and 0.75 mm.
3. The multi-layered material according to claim 1 , having a protection value against arc flash ATPV higher than 45 cal/cm 2 .
4. A process for the manufacture of the multi-layered material according to claim 1 , comprising:
I. preparing a solution of silicone rubber in an organic solvent thereof, adding iron (III) oxide micro-powder, transferring a first half of the so obtained solution in an open container having width and length equal to those of the sample material to be prepared;
II. positioning in the container of step i) above, a fabric of flame-retardant fibres to cover said first half of the solution;
III. adding to a second half of the solution obtained in step i) above, glass hollow microspheres, followed by mixing and transferring of the so obtained mixture on said flame-retardant fabric of step ii);
IV. partially evaporating said organic solvent from said container by air drying;
V. positioning a fabric of para-aramid fibres to cover the underlying layers, and completing the evaporation of the solvent.
5. An article or a personal protective equipment against arc flash coated by or manufactured with the multi-layered material of claim 1 .
6. The article or personal protective equipment of claim 5 , consisting of a glove completely manufactured with said multi-layered material.