Hydrodesulfurization catalyst for hydrocarbon oil and method for manufacturing hydrodesulfurization catalyst
Provided is a hydrodesulfurization catalyst for hydrocarbon oil, the catalyst comprising: an inorganic oxide carrier comprising Si, Ti and Al; and at least one metal component, carried on the inorganic oxide carrier, being selected from the group consisting of group 6 elements, group 8 elements, group 9 elements and group 10 elements, wherein the content of Al in the inorganic oxide carrier is 50% by mass or higher in terms of Al 2 O 3 ; the content of Si therein is 1.0 to 10% by mass in terms of SiO 2 ; and the content of Ti therein is 12 to 28% by mass in terms of TiO 2 ; and in the inorganic oxide carrier, the absorption edge wavelength of an absorption peak from Ti is 364 nm or shorter as measured by ultraviolet spectroscopy.
1. A hydrodesulfurization catalyst for hydrocarbon oil, the catalyst comprising:
an inorganic oxide carrier comprising Si, Ti and Al; and
at least one metal component, carried on the inorganic oxide carrier, being selected from the group consisting of group 6 elements, group 8 elements, group 9 elements and group 10 elements,
wherein a content of Al in the inorganic oxide carrier is 50% by mass or higher in terms of Al 2 O 3 ; a content of Si therein is 1.0 to 10% by mass in terms of SiO 2 ; and a content of Ti therein is 12 to 28% by mass in terms of TiO 2 ; and
in the inorganic oxide carrier, an absorption edge wavelength of an absorption peak from Ti is 364 nm or shorter as measured by ultraviolet spectroscopy.
2. The hydrodesulfurization catalyst according to claim 1 , wherein a specific surface area (SA) of the hydrodesulfurization catalyst is 150 m 2 /g or larger, and a pore volume (PV) thereof is 0.30 ml/g or larger.
3. The hydrodesulfurization catalyst according to claim 1 , wherein the metal component comprises at least one selected from the group consisting of molybdenum, tungsten, cobalt and nickel.
4. The hydrodesulfurization catalyst according to claim 1 , wherein a content of the metal component is 1 to 35% by mass in terms of oxide.
5. A method for producing a hydrodesulfurization catalyst, the method comprising:
mixing a first aqueous solution comprising a mineral acid salt of titanium and an acidic aluminum salt with a second aqueous solution comprising a basic aluminum salt to make a mixed liquid of pH 6.5 to 9.5 to thereby obtain a carrier precursor deposited in the mixed liquid, wherein a period of time is 60 min or shorter from when the mineral acid salt of titanium and the acidic aluminum salt are mixed until when the first aqueous solution and the second aqueous solution are mixed;
calcining the carrier precursor to obtain a carrier;
making the carrier to carry at least one metal component selected from the group consisting of group 6 elements, group 8 elements, group 9 elements and group 10 elements to obtain the hydrodesulfurization catalyst,
wherein the first aqueous solution and/or the second aqueous solution comprises a silicate ion, and
thereby producing a hydrodesulfurization catalyst of claim 1 .
6. The method according to claim 5 , wherein the first aqueous solution is prepared at 60° C. or lower.