Polar additive for the synthesis of copolymers of vinylaromatic monomer and conjugated diene monomer having high vinylaromatic and low vinyl contents
The present invention relates to the use of N,N′,N″-substituted hexahydro-1,3,5-triazine in the anionic polymerization of conjugated diene monomer and vinylaromatic monomer. Use of this polar additive produces copolymers having both high vinylaromatic and low vinyl contents, while the blockiness of the vinylaromatic unit can be tailored.
1. A copolymer based on conjugated diene monomer and vinylaromatic monomer, the copolymer having
(a) a content of vinylaromatic monomer from about 35 to about 55 weight percent, based on total weight of polymer;
(b) a content of vinylaromatic monomer blocks with more than 4 repeating units from about 0.01 to about 12 weight percent, based on total vinylaromatic monomer content; and
(c) a vinyl content from more than 8 to about 35 weight percent, based on total conjugated diene polymerized fraction.
2. The copolymer of claim 1 , wherein the (a) content of vinylaromatic monomer is from about 40 to about 55 weight percent.
3. The copolymer of claim 1 , wherein the (b) content of vinylaromatic monomer blocks with more than 4 repeating units is from about 0.05 to about 12 weight percent, based on total vinylaromatic monomer content.
4. The copolymer of claim 1 , wherein the (c) vinyl content is from about 10 to about 35 weight percent, based on total conjugated diene polymerized fraction.
5. The copolymer of claim 1 , wherein Mw/Mn of the uncoupled product is in a range of from about 1.01 to about 3.0.
6. A method for preparing a rubber comprising vulcanizing the elastomeric copolymer according to claim 1 in the presence of one or more vulcanizing agents.
7. A rubber as obtainable according to the method of claim 6 .
8. A rubber composition comprising x) a rubber component comprising the rubber according to claim 7 .
9. The rubber composition according to claim 8 , further comprising y) one or more fillers.
10. The rubber composition according to claim 9 , wherein the amount of filler component y) is 10 to 150 parts by mass relative to 100 parts by mass of the rubber component x) (phr).
11. The rubber composition according to claim 8 wherein the rubber component x) also comprises one or more further rubbery polymers.
12. A tire component comprising the rubber composition according to claim 8 .
13. A tire comprising the tire component of claim 12 .
14. The copolymer of claim 3 , wherein the (b) content of vinylaromatic monomer blocks with more than 4 repeating units is from about 0.1 to about 12 weight percent, based on total vinylaromatic monomer content.
15. The copolymer of claim 14 , wherein the (b) content of vinylaromatic monomer blocks with more than 4 repeating units is from about 0.1 to about 6 weight percent, based on total vinylaromatic monomer content.
16. The copolymer of claim 15 , wherein the (b) content of vinylaromatic monomer blocks with more than 4 repeating units is from about 0.1 to about 3 weight percent, or from about 0.1 to about 2.5 weight percent, each based on total vinylaromatic monomer content.
17. The copolymer of claim 4 , wherein the (c) vinyl content is from about 18 to about 27 weight percent, based on total conjugated diene polymerized fraction.
18. The copolymer of claim 5 , wherein Mw/Mn of the uncoupled product is in a range of from about 1.01 to about 1.2.
19. The rubber composition according to claim 9 , wherein the filler is selected from the group consisting of silica, carbon black, and mixtures thereof.
20. The rubber composition according to claim 10 , wherein the amount of component y) is 30 to 130 phr.
21. The rubber composition according to claim 11 , wherein the further rubbery polymer is selected from the group consisting of natural rubber, synthetic isoprene rubber, butadiene rubber, ethylene-α-olefin copolymer rubber, ethylene-α-olefin-diene copolymer rubber, acrylonitrile-butadiene copolymer rubber, chloroprene rubber and halogenated butyl rubber.
22. The tire component of claim 12 , wherein the tire component is a tire tread.