Stimuli-responsive micro-reservoirs for release of encapsulants
This invention relates to polymer-based partially-open, hollow reservoirs in the nano-size to micro-size range that encapsulate an additive, which can be released from the reservoirs using specific event stimuli such as reduction-oxidation and voltage change, or at will, using the same stimuli. This invention also relates to method preparing such reservoirs, and for releasing the additive. This invention further relates to matrix that comprises such reservoirs and the method of preparing such matrix. This invention also relates to applications, for example in corrosion inhibition, lubrication, and adhesion, that benefit from using such a controlled release of an additive.
1. A plurality of partially-open, hollow reservoirs
comprising at least one encapsulant;
a polymer comprising at least one conducting polymer;
wherein the plurality of partially-open, hollow reservoirs have at least one opening on their surface, such that the average opening area, in the aggregate, of said plurality of partially-open, hollow reservoirs is from about 0.25% to about 50% of the surface area in the aggregate of said plurality of partially-open, hollow reservoirs;
wherein the average size of said plurality of partially-open, hollow reservoirs is in the range of from about 200 nm to about 10,000 nm;
wherein said at least one encapsulant releasably resides within said plurality of partially-open, hollow reservoirs.
2. The plurality of partially-open, hollow reservoirs as recited in claim 1 , wherein said at least one conducting polymer is selected from polyaniline-based polymer, polyaniline-based polymer derivatives, polypyrrole, polypyrrole based polymer, polypyrrole based polymer's derivatives, blends thereof, and mixtures thereof.
3. The plurality of partially-open, hollow reservoirs as recited in claim 2 , wherein said conducting polymer is the polyaniline-based polymer, comprising at least one of polyaniline, poly-o-toluidine, poly-o-methoxyaniline, poly-o-ethylaniline, and poly-2-ethoxyaniline.
4. The plurality of partially-open, hollow reservoirs as recited in claim 3 , wherein the plurality of partially-open, hollow reservoirs comprises the at least one polyaniline-based polymer in its base form, in its salt form, or in a blend of its base form and its salt form.
5. The plurality of partially-open, hollow reservoirs, as recited in claim 4 , wherein the at least one polyaniline-based polymer is in its emeraldine form, in its leucoemeraldine form, or in its pernigraniline form, or a combination thereof.
6. The plurality of partially-open, hollow reservoirs as recited in claim 1 , wherein said encapsulant is selected from the group consisting of a corrosion inhibiting additive, a lubricant additive, an adhesive additive, a biocide additive, an antifouling additive, a pesticide additive, a drug delivery additive, a corrosion sensor additive, a fragrance releasing additive, a catalyst additive, an ink additive, a dye additive, an enzyme additive, a reactant additive, and combinations thereof.
7. The plurality of partially-open, hollow reservoirs as recited in claim 6 , wherein said corrosion inhibiting additive is selected from (a) an organic compound containing an amino group or carboxy group or salts of carboxylic acids, organic sulfides, heterocyclic rings, substituted aromatic rings, organic phosphates and phosphonic acids, quaternary ammonium compounds, imidazolines, aldehydes, sulfoxides, carboxylic acids, mercaptocarboxylic acids, imidazoles, oximes, azoles, tannins, substituted phenols, quinoline and quinolone compounds, substituted quinolines and quinalizarin, pyridinium group, pyrazine group, an azole derivative, and, one or more schiffs bases; (b) an organic compound containing one or more anions selected from the group comprising polyphosphate and its derivatives, nitrite, silicate, molybdate, and polymolybdate and its derivatives, vanadate and polyvanadate and its derivatives; and (c) an organic or inorganic compound comprising one or more cations selected from the group comprising lanthanides, magnesium, calcium, titanium, zirconium, yttrium, chromium and silver; combinations of components within each corrosion inhibiting additive group (a), (b), and (c); and combinations between one or more components of each additive group (a), (b), and (c).
8. The plurality of partially-open, hollow reservoirs as recited in claim 6 , wherein said encapsulant is a lubricant additive selected from: (i) antioxidant additives selected from phenols and its derivatives, aromatic and aryl amines; (ii) anti-wear additives selected from metal alkyltiophosphate; (iii) dispersants selected from of phenates, sulfurized phenates, salicylates, naphthenates, stearates, carbamates, thiocarbamates, phosphorus derivatives; combinations of components within each lubricant additive group (i), (ii), and (iii); and combinations between one or more components of each lubricant additive group (i), (ii), and (iii).
9. The plurality of partially-open, hollow reservoirs as recited in claim 6 , wherein said encapsulant is an adhesive additive selected from the following corrosion inhibitor encapsulants:
chromate compositions, phosphates, silicates, nitrates, benzoates, mercaptobenzothiazoles, sodium molybdate formulations, phosphonic acids combined with amines, and combinations thereof.
10. A matrix comprising the plurality of partially-open, hollow reservoirs as recited in claim 6 .
11. The plurality of partially-open, hollow reservoirs as recited in claim 1 , wherein said partially-open, hollow reservoirs are nominally spherical-shaped hollow reservoirs, nominally rod-shaped hollow reservoirs, irregular-shaped hollow reservoirs, or a hollow micro-particles with more than one opening.
12. A process for preparing the plurality of the partially-open, hollow reservoirs as recited in claim 3 , devoid of any encapsulant, wherein said conducting polymer is the polyaniline-based polymer, comprising the step of polymerizing a monomer of the polyaniline-based polymer by aqueous oxidative polymerization.
13. A process for preparing the plurality of partially-open, hollow reservoirs as recited in claim 1 ; comprising the steps of:
(A1) preparing a plurality of partially-open, hollow reservoirs devoid of any encapsulant; and
(A2) encapsulating the at least one encapsulant by (a) solvent evaporation; or (b) precipitation method; OR
comprising the step of:
(BI) in-situ encapsulation of encapsulant during the polymerization process of partially-open, hollow reservoirs.
14. The process as recited in claim 13 , wherein said conducting polymer is at least one polyaniline-based polymer.
15. The process as recited in claim 14 , wherein said at least one polyaniline-based polymer is in its base form, or in its salt form, or in a blend of its base form and its salt form.
16. The process as recited in claim 15 , wherein said at least one polyaniline-based polymer is in its emeraldine form or its leucoemeraldine form or pernigraniline form.
17. The process as recited in claim 13 , wherein said encapsulant is selected from the group consisting of a corrosion inhibiting additive, a lubricant additive, an adhesive additive, a biocide additive, an antifouling additive, a pesticide additive, a drug delivery additive, a corrosion sensor additive, a fragrance releasing additive, a catalyst additive, an ink additive, a dye additive, an enzyme additive, a reactant additive, and combinations thereof.
18. A process for preparing a matrix comprising the plurality of partially-open, hollow reservoirs as recited in claim 1 , comprising the steps of:
(1) contacting said POHR with said matrix, and optionally
(2) mixing said POHR in said matrix.
19. The process as recited in claim 18 , wherein said matrix is a paint or a coating, and said encapsulant is a corrosion inhibitor.
20. A process for preparing the plurality of partially-open, hollow reservoirs as re-cited in claim 1 , comprising the step of in-situ encapsulation of the at least one encapsulant inside the plurality of the partially-open, hollow reservoirs during synthesis of said plurality of the partially-open hollow reservoirs.
21. A process for releasing the at least one encapsulant from the plurality of the partially-open, hollow reservoirs as recited in claim 1 , comprising the step of providing external stimuli to the plurality of the partially-open, hollow reservoirs; wherein the external stimuli is at least one of the following:
(1) changing the pH of the environment of the plurality of the partially-open, hollow reservoirs;
(2) changing the redox potential of the plurality of the partially-open, hollow reservoirs;
(3) changing the oxidation state of the plurality of the partially-open, hollow reservoirs;
(4) mechanically damaging the plurality of the partially-open, hollow reservoirs;
(5) changing the voltage applied to the plurality of the partially-open, hollow reservoirs; and
(6) changing the electrochemical potential of the plurality of the partially-open, hollow reservoirs.
22. A process for inhibiting corrosion in metal, comprising the step of coating said metal with a coating matrix comprising the partially-open, hollow reservoirs as recited in claim 1 , wherein said at least one encapsulant comprises at least one corrosion inhibitor.
23. The process as recited in claim 22 , wherein said at least one corrosion inhibitor is selected from (a) an organic compound containing an amino group or carboxy group or salts of carboxylic acids, organic sulfides, heterocyclic rings, substituted aromatic rings, organic phosphates and phosphonic acids, quaternary ammonium compounds, imidazolines, aldehydes, sulfoxides, carboxylic acids, mercaptocarboxylic acids, imidazoles, oximes, azoles, tannins, substituted phenols, quinoline and quinolone compounds, substituted quinolines and quinalizarin, pyridinium group, pyrazine group, an azole derivative, and, one or more schiffs bases; (b) an organic com-pound containing one or more anions selected from the group comprising polyphosphate and its derivatives, nitrite, silicate, molybdate, and polymolybdate and its derivatives, vanadate and poly-vanadate and its derivatives; and (c) an organic or inorganic compound comprising one or more cations selected from the group comprising lanthanides, magnesium, calcium, titanium, zirconium, yttrium, chromium and silver; combinations of components within each corrosion inhibiting additive group (a), (b), and (c); and combinations between one or more components of each additive group (a), (b), and (c).
24. The process as recited in claim 22 , wherein the matrix coating is latexes, amino resins, polyurethanes, epoxies, phenolic resins, acrylic resins, polyester resins, alkyd resins, polysulfide resins, polyaspartic, polyurea, polylactones, adducts of amines, polyimide, polycarbonate, polyvinyl and halogenated polymer resins.
25. The process as recited in claim 22 , wherein said metal is part of an automotive, a refinish part, a marine vehicle part, a part of an equipment, a metal cladding part, a part of any other vehicle, a part for any other vehicle, a part of a flying object, part of a decorative piece, industrial machinery, industrial machinery parts, pipe parts, tank parts, and bridge parts, coils, architecture and architecture parts, metal equipment and structures used in the power sector, metal equipment and structures used in the energy sector, and metal equipment and structures used in transportation sectors.
26. The process as recited in claim 18 , wherein said matrix is a lubricant and said encapsulant is a lubricant additive selected from: (i) antioxidant additives selected from phenols and its derivatives, aromatic and aryl amines; (ii) anti-wear additives selected from metal alkyltiophosphate; (iii) dispersants selected from of phenates, sulfurized phenates, salicylates, naphthenates, stearates, carbamates, thiocarbamates, phosphorus derivatives; combinations of components within each lubricant additive group (i), (ii), and (iii); and combinations between one or more components of each lubricant additive group (i), (ii), and (iii).
27. The process as recited in claim 18 , wherein said matrix is an adhesive, wherein said encapsulant is an adhesive additive selected from the following corrosion inhibitor encapsulants:
chromate compositions, phosphates, silicates, nitrates, benzoates, mercaptobenzothiazoles, sodium molybdate formulations, phosphonic acids combined with amines, and combinations thereof.