Oxide semiconductor thin-film and thin-film transistor consisted thereof
The present application discloses an oxide semiconductor thin-film and a thin-film transistor consisted thereof. The oxide semiconductor thin-film is fabricated by doping a certain amount of rare-earth oxide (RO) as light stabilizer to metal oxide (MO) semiconductor. The thin-film transistor comprising a gate electrode, a channel layer consisted by the oxide semiconductor thin-film, a source and drain electrode; the thin-film transistor employing etch-stop structure, a back-channel etch structure or a top-gate self-alignment structure.
1. An oxide semiconductor thin-film, wherein, the oxide semiconductor thin-film is fabricated from a (MO) x (RO) y semiconductor material by doping an amount of rare-earth oxide (RO) as a light stabilizer to a metal oxide (MO) semiconductor, wherein, 0.8≤x<1, 0.012≤y≤0.2, x+y=1;
the M in the metal oxide semiconductor consists of one or more elements selected from the group consisting of In, Zn, Ga, Sn, and combinations thereof;
the R in the rare-earth oxide is at least one element selected from the group consisting of Pr, Tb, Dy, and Yb.
2. The oxide semiconductor thin-film of claim 1 , wherein, the M in the metal oxide semiconductor is a combination of Zn with one or two elements selected from Sn, In and Ga.
3. The oxide semiconductor thin-film of claim 2 , wherein, the metal oxide semiconductor is one selected from the group consisting of indium-zinc-oxide, indium-gallium-zinc-oxide, indium-tin-zinc-oxide and tin-zinc-oxide.
4. The oxide semiconductor thin-film of claim 3 , wherein, ingredient mole ratio of In 2 O 3 :ZnO is 2:1 in the indium-zinc-oxide.
5. The oxide semiconductor thin-film of claim 3 , wherein, ingredient mole ratio of In 2 O 3 :Ga 2 O 3 :ZnO is 2:1:2 in the indium-gallium-zinc-oxide.
6. The oxide semiconductor thin-film of claim 3 , wherein, ingredient mole ratio of In 2 O 3 :SnO 2 :ZnO is 1:1:1 in the indium-tin-zinc-oxide.
7. The oxide semiconductor thin-film of claim 3 , wherein, ingredient mole ratio of ZnO:SnO 2 is 2:1 in the tin-zinc-oxide.
8. The oxide semiconductor thin-film of claim 1 , wherein, the (MO) x (RO) y semiconductor material is one selected from the group consisting of praseodymium-doped indium-zinc-oxide, terbium-doped indium-gallium-zinc-oxide, dysprosium-doped indium-tin-zinc-oxide, and ytterbium-doped tin-zinc-oxide.
9. The oxide semiconductor thin-film of claim 1 , wherein, the oxide semiconductor thin-film is fabricated by sputtering in Ar and O 2 mixture gas with an oxygen volume ratio at 0.1 to 0.6.
10. The oxide semiconductor thin-film of claim 1 , wherein, the oxide semiconductor thin-film is fabricated by sputtering in Ar and O 2 mixture gas with an oxygen volume ratio at 0.2 to 0.3.
11. The oxide semiconductor thin-film of claim 1 , wherein, the oxide semiconductor thin-film is fabricated by a solution process.
12. A thin-film transistor, comprising a channel layer consisted by an oxide semiconductor thin-film, wherein,
the oxide semiconductor thin-film is fabricated from a (MO) x (RO) y semiconductor material by doping an amount of rare-earth oxide (RO) as a light stabilizer to a metal oxide (MO) semiconductor, wherein, 0.8≤x<1, 0.012≤y≤0.2, x+y=1;
the M in the metal oxide semiconductor consists of one or more elements selected from In, Zn, Ga, Sn, and combinations thereof;
the R in the rare-earth oxide is at least one element selected from the group consisting of Pr, Tb, Dy, and Yb.
13. The thin-film transistor of claim 12 , further comprising: a substrate, a gate electrode, a gate insulator layer, an etch-stop layer, a source and drain electrode; wherein, the thin-film transistor employs an etch-stop structure.
14. The thin-film transistor of claim 12 , further comprising: a substrate, a gate electrode, a gate insulator layer, a source and drain electrode; wherein, the thin-film transistor employs a back-channel etch structure.
15. The thin-film transistor of claim 14 , wherein, the source and drain electrode is patterned under etchant of hydrogen peroxide based etching solution or aluminic based etching solution.
16. The thin-film transistor of claim 12 , further comprising: a substrate, a buffer layer, a gate insulator layer, a gate electrode, an interval layer, a source and drain electrode; wherein, the thin-film transistor employs a top-gate self-alignment structure.
17. The thin-film transistor of claim 16 , wherein, the substrate is a flexible substrate made from polyimide, polyethylene naphthalate, polyethylene terephthalate, polyethylene, polypropylene, polystyrene, or polyethersulfone.
18. The oxide semiconductor thin-film of claim 1 , having an indirect band-gap.
19. The thin-film transistor of claim 12 , wherein the oxide semiconductor thin-film has an indirect band-gap.