Reactive inorganic coatings for agricultural fertilizers
The invention relates to a coated granular fertilizer, preferably wherein granules are sulfate-based or phosphate-based. When sulfate based granules, as in ammonium sulfate, the coating substance is an inorganic salt of alkaline earth elements, preferably calcium, such that when applied to the surface of fertilizers, forms calcium sulfate, preferably a calcium sulfate-dihydrate, as a protective coating. For a reactive coating of a thiosulfate, free sulfuric acid present on the granule reacts to provide an elemental sulfur coating. For ammonium phosphate-based granules, coatings may comprise compounds of Ca ++ , Al +++ and/or Fe +++ salts thereby forming a calcium, an aluminum, an iron, or mixed cation phosphate protective coating. Thiosulfate is also effective with phosphate based granules which are manufactured with sulfuric acid. Granules coated according to the disclosure have advantageous properties as the coating can be applied in a specified and sparing manner due to its tendency to adhere to surfaces during the reaction. Coated fertilizer granules of the disclosure are also advantageous in that, with regard to the applied amount of coating, they provide increased resistance to dusting in long term warehouse storage, to moisture uptake and to oxidative heating. Coating components also add nutrients to plants that can provide nutrients over a longer period of time such as a slow-release characteristic.
1. A method of coating fertilizer granules comprising:
providing fertilizer granules containing organic material and an acid;
contacting the fertilizer granules at an acidic pH with an inorganic compound, wherein the inorganic compound chemically reacts with the acid of the fertilizer granules forming a coating on the fertilizer granules, wherein the coating comprises aluminum, iron, aluminum-calcium sulfate, ferrous ammonium phosphate, sulfur, and/or an aluminum-iron complex; and
drying the coated fertilizer granules forming dried and coated granules.
2. The method of claim 1 , wherein the acid comprises sulfuric acid, phosphoric acid, nitric acid, and/or hydrochloric acid.
3. The method of claim 1 , wherein the acidic pH is less than about 6.8.
4. The method of claim 1 , wherein the acidic pH is less than about 6.0.
5. The method of claim 1 , wherein the inorganic compound comprises an alkaline metal, ammonium thiosulfate, potassium thiosulfate, and/or sodium thiosulfate.
6. The method of claim 1 , wherein the inorganic compound contains a cationic component and the fertilizer granules contain an anionic component.
7. The method of claim 6 , wherein the anionic component comprises chloride ions (Cl − ), nitrate ions (NO 3 − ), ammonium nitrate ions (NH 4 NO 3 − ), hydroxide ions (OH) − ), and/or acetate ions (CH 3 COO − ).
8. The method of claim 6 , wherein the cationic component comprises barium ions, calcium ions, magnesium ions, aluminum ions, polyaluminum ions, iron ions, and/or sulfur ions.
9. The method of claim 6 , wherein the cationic component comprises calcium ions and the anionic component comprises chloride ions.
10. The method of claim 1 , wherein contacting comprises spraying an aqueous solution of the inorganic compound on surfaces of the fertilizer granules.
11. The method of claim 1 , wherein the coating comprises from about 4 to about 40 pounds per ton of dried granules.
12. The method of claim 1 , wherein the coating comprises from about 10 to about 20 pounds per ton of dried granules.
13. The method of claim 1 , wherein the dried and coated granules comprise about 92% to about 100% solids.
14. The method of claim 1 , wherein the dried and coated granules comprise about 96% to about 99% solids.
15. The method of claim 1 , wherein the dried and coated granules comprise about 98% to about 99% solids.
16. The method of claim 1 , wherein the dried and coated granules have reduced dust formation as compared to fertilizer granules that have not been so processed.
17. The method of claim 1 , wherein the dried and coated granules are less absorbent to humidity as compared to fertilizer granules that have not been so processed.
18. The method of claim 1 , wherein the dried and coated granules are resistant to self-heating as compared to fertilizer granules that have not been so processed.
19. The method of claim 1 , wherein the dried and coated granules have a reduced odor as compared to fertilizer granules that have not been so processed.
20. The method of claim 1 , wherein the dried and coated granules have a slow-release nutrient profile.
21. The method of claim 20 , wherein the slow-release nutrient profile comprises a reduced rate, reduced amount, and/or differential release of one or more nutrients from the dried and coated granules.
22. The method of claim 1 , wherein the dried and coated granules have an enhanced release of one or more nutrients.
23. The method of claim 22 , wherein the one or more nutrients comprise nitrogen, phosphorus, potassium, sulfur, iron, organics, or a combination thereof.
24. The method of claim 1 , further comprising adding micronutrients to the fertilizer granules.
25. The method of claim 24 , wherein the micronutrients comprise boron, calcium, copper, magnesium, manganese, molybdenum, sulfur, zinc and/or combinations thereof.
26. The method of claim 1 , wherein the fertilizer granules contain organic materials that are chemically bound to inorganic nutrients by covalent bonds, noncovalent bonds, electrostatic bonds, hydrogen bonds and/or combinations thereof.
27. The method of claim 1 , wherein the contacting further comprises a surfactant.
28. The method of claim 27 , wherein the surfactant comprises dodecylbenzyl sulfonic acid (DBSA), an ethoxylated alcohol of C10-C16, sodum lauryl ether sulfate, amine oxide, methyl salicylate, coco betaine, an anionic, cationic, or nonionic surfactants, or mixtures thereof.
29. Dried and coated granules made by the method of claim 1 .
30. A method of coating fertilizer containing organic material comprising:
providing fertilizer comprised of organic materials that contain exposed chloride ions (Cl − ), nitrate ions (NO 3 − ), ammonium nitrate ions (NH 4 NO 3 − ), hydroxide ions (OH) − ), and/or acetate ions (CH 3 COO − );
providing an inorganic compound that contains ions selected from the group consisting of Ca, Mg, Mn, Fe, Al, and Zn;
contacting the fertilizer at an acidic pH with the inorganic compound forming a coating on the fertilizer, wherein the coating comprises aluminum, iron, aluminum-calcium sulfate, ferrous ammonium phosphate, sulfur, and/or an aluminum-iron complex; and
drying the coated fertilizer.
31. The method of claim 30 , wherein the coating comprises (Al)Cl 3 , (Al)chlorohydrate, polyaluminum chloride, (Ca)NH 4 NO 3 , (Ca)Cl 2 , (Fe)Cl 3 , FeSO 4 -7H 2 O, (Fe) 3 (SO 4 ) 2 , (Mg)SO 4 , (Mg)Cl 2 , (Mn)Cl 2 , (Mn)NH 4 PO 4 , (Ca) 3 (PO 4 ) 2 , monocal (Ca)(H 2 PO 4 ) 2 H 2 O, and/or dical (Ca 2 )(H 2 PO 4 ) 4 , and/or elemental sulfur.
32. The method of claim 30 , wherein the acidic pH is less than about 6.8.
33. The method of claim 30 , wherein the coated fertilizer, as compared to fertilizer not so processed:
has reduced dust formation;
is less absorbent to humidity;
is resistant to self-heating; and/or
has a reduced odor.
34. The method of claim 30 , wherein the contacting further comprises a surfactant.
35. The method of claim 34 , wherein the surfactant comprises dodecylbenzyl sulfonic acid (DBSA), an ethoxylated alcohol of C10-C16, sodium lauryl ether sulfate, amine oxide, coco betaine, an anionic, cationic, or nonionic surfactants, or mixtures thereof.
36. A method of coating fertilizer granules comprising:
providing fertilizer granules containing organic material and an acid;
contacting the fertilizer granules at an acidic pH with an inorganic compound and a surfactant, wherein the inorganic compound chemically reacts with the acid of the fertilizer granules forming a coating on the fertilizer granules, wherein the coating comprises aluminum, iron, aluminum-calcium sulfate, calcium sulfate, ferrous ammonium phosphate, sulfur, and/or an aluminum-iron complex; and
drying the coated fertilizer granules forming dried and coated granules.
37. The method of claim 36 , wherein the acid comprises sulfuric acid, phosphoric acid, nitric acid, and/or hydrochloric acid.
38. The method of claim 36 , wherein the acidic pH is less than about 6.8.
39. The method of claim 36 , wherein the acidic pH is less than about 6.0.
40. The method of claim 36 , wherein the inorganic compound contains a cationic component and the fertilizer granules contain an anionic component.
41. The method of claim 40 , wherein the anionic component comprises chloride ions (Cl − ), nitrate ions (NO 3 − ), ammonium nitrate ions (NH 4 NO 3 − ), hydroxide ions (OH) − ), and/or acetate ions (CH 3 COO − ).
42. The method of claim 40 , wherein the cationic component comprises calcium ions and the anionic component comprises chloride ions.
43. The method of claim 36 , wherein contacting comprises spraying an aqueous solution of the inorganic compound on surfaces of the fertilizer granules.
44. The method of claim 36 , wherein the coating comprises from about 4 to about 40 pounds per ton of dried granules.
45. The method of claim 36 , wherein the coating comprises from about 10 to about 20 pounds per ton of dried granules.
46. The method of claim 36 , wherein the dried and coated granules comprise about 92% to about 100% solids.
47. The method of claim 36 , wherein the dried and coated granules comprise about 96% to about 99% solids.
48. The method of claim 36 , wherein the dried and coated granules comprise about 98% to about 99% solids.
49. The method of claim 36 , wherein the dried and coated granules have reduced dust formation as compared to fertilizer granules that have not been so processed.
50. The method of claim 36 , wherein the dried and coated granules are less absorbent to humidity as compared to fertilizer granules that have not been so processed.
51. The method of claim 36 , wherein the dried and coated granules are resistant to self-heating as compared to fertilizer granules that have not been so processed.
52. The method of claim 36 , wherein the dried and coated granules have a reduced odor as compared to fertilizer granules that have not been so processed.
53. The method of claim 36 , wherein the dried and coated granules have a slow-release nutrient profile.
54. The method of claim 53 , wherein the slow-release nutrient profile comprises a reduced rate, reduced amount, and/or differential release of one or more nutrients from the dried and coated granules.
55. The method of claim 36 , wherein the dried and coated granules have an enhanced release of one or more nutrients.
56. The method of claim 55 , wherein the one or more nutrients comprise nitrogen, phosphorus, potassium, sulfur, iron, organics, or a combination thereof.
57. The method of claim 36 , further comprising adding micronutrients to the fertilizer granules.
58. The method of claim 57 , wherein the micronutrients comprise boron, calcium, copper, magnesium, manganese, molybdenum, sulfur, zinc and/or combinations thereof.
59. The method of claim 36 , wherein the fertilizer granules contain organic materials that are chemically bound to inorganic nutrients by covalent bonds, noncovalent bonds, electrostatic bonds, hydrogen bonds and/or combinations thereof.
60. The method of claim 36 , wherein the surfactant comprises dodecylbenzyl sulfonic acid (DBSA), an ethoxylated alcohol of C10-C16, sodium lauryl ether sulfate, amine oxide, coco betaine, an anionic, cationic, or nonionic surfactants, or mixtures thereof.
61. A method of coating fertilizer containing organic material comprising:
providing fertilizer comprised of organic materials that contain exposed chloride ions (Cl − ), nitrate ions (NO 3 − ), ammonium nitrate ions (NH 4 NO 3 − ), hydroxide ions (OH) − ), and/or acetate ions (CH 3 COO − );
providing an inorganic compound that contains ions selected from the group consisting of Ca, Mg, Mn, Fe, Al, and Zn;
contacting the fertilizer at an acidic pH with the inorganic compound and a surfactant forming a coating on the fertilizer, wherein the coating comprises aluminum, iron, aluminum-calcium sulfate, calcium sulfate, ferrous ammonium phosphate, sulfur, and/or an aluminum-iron complex; and
drying the coated fertilizer.
62. The method of claim 61 , wherein the acidic pH is less than about 6.8.
63. The method of claim 61 , wherein the coated fertilizer, as compared to fertilizer not so processed:
has reduced dust formation;
is less absorbent to humidity;
is resistant to self-heating; and/or
has a reduced odor.
64. The method of claim 61 , wherein the surfactant comprises dodecylbenzyl sulfonic acid (DBSA), an ethoxylated alcohol of C10-C16, sodium lauryl ether sulfate, amine oxide, methyl salicylate, coco betaine, an anionic, cationic, or nonionic surfactants, or mixtures thereof.