Friction member, friction material composition, friction material, and vehicle
The present invention relates to a friction member comprising a friction material and a back metal, wherein the friction material comprises no copper, or has a copper content of less than 0.5% by mass in terms of a copper element even if the friction material comprises copper, the friction material comprises magnesium oxide and a carbon material comprising graphite and coke, the carbon material is obtained by blending in a combination of a coarse-grained material and a fine-grained material, an average particle diameter of the coarse-grained material is 100 to 600 μm, and an average particle diameter of the fine-grained material is less than 100 μm.
1. A friction member comprising a friction material and a back metal, wherein
the friction material comprises no copper, or has a copper content of less than 0.5% by mass in terms of a copper element even if the friction material comprises copper,
the friction material comprises magnesium oxide and a carbon material comprising graphite and coke,
the carbon material is obtained by blending in a combination of a coarse-grained material and a fine-grained material,
the friction material comprises the graphite and the coke as the coarse-grained material, and comprises the coke as the fine-grained material,
an average particle diameter of the coarse-grained material is 100 to 600 μm, and
an average particle diameter of the fine-grained material is less than 100 μm,
a content of the coarse-grained material of the graphite is 1 to 12% by mass based on a total amount of the friction material,
a content of the coarse-grained material of the coke is 1 to 12% by mass based on the total amount of the friction material,
a content of the fine-grained material of the coke is 1 to 12% by mass based on the total amount of the friction material, and
a total content of the graphite and the coke is 4 to 15% by mass based on the total amount of the friction material.
2. The friction member according to claim 1 , wherein a content ratio of the coarse-grained material to the fine-grained material [coarse-grained material/fine-grained material] in the friction material is 10/90 to 95/5 on a mass basis.
3. The friction member according to claim 1 , wherein the friction material comprises the graphite as the coarse-grained material comprises the coke as the fine grained material.
4. The friction member according to claim 1 , wherein a content of the magnesium oxide in the friction material is 3 to 13% by mass based on a total amount of the friction material.
5. The friction member according to claim 1 , wherein the friction material further comprises 2 to 10% by mass of zinc oxide based on a total amount of the friction material.
6. A vehicle equipped with the friction member according to claim 1 .
7. A friction material composition comprising no copper, or having a copper content of less than 0.5% by mass in terms of a copper element even if the friction material composition comprises copper, wherein
the friction material composition comprises magnesium oxide and a carbon material comprising graphite and coke,
the carbon material is obtained by blending in a combination of a coarse-grained material and a fine-grained material,
the friction material composition comprises the graphite and the coke as the coarse-grained material, and comprises the coke as the fine-grained material,
an average particle diameter of the coarse-grained material is 100 to 600 μm, and
an average particle diameter of the fine-grained material is less than 100 μm,.
a content of the coarse-grained material of the graphite is 1 to 12% by mass based on a total amount of the friction material composition,
a content of the coarse-grained material of the coke is 1 to 12% by mass based on the total amount of the friction material composition,
a content of the fine-grained material of the coke is 1 to 12% by mass based on the total amount of the friction material composition, and
a total content of the graphite and the coke is 4 to 15% by mass based on the total amount of the friction material composition.
8. The friction material composition according to claim 7 , wherein a content ratio of the coarse-grained material to the fine-grained material [coarse-grained material/fine-grained material] is 10/90 to 95/5 on a mass basis.
9. The friction material composition according to claim 7 , comprising the graphite as the coarse-grained material.
10. The friction material composition according to claim 7 , wherein a content of the magnesium oxide is 3 to 13% by mass based on a total amount of the friction material composition.
11. The friction material composition according to claim 7 , further comprising 2 to 10% by mass of zinc oxide based on a total amount of the friction material composition.
12. A friction material comprising the friction material composition according to claim 7 .