Magnetic toner
A magnetic toner comprising a magnetic toner particle including a binder resin, a magnetic body and a crystalline polyester, wherein the dielectric loss tangent at 100 kHz is 1.0×10 −2 or more, a variation coefficient CV3 of an occupied area ratio of the magnetic body when a cross section of the magnetic toner particle is divided by a square grid having a side of 0.8 μm in cross-sectional observation of the magnetic toner particle using a transmission electron microscope TEM is from 30.0% to 80.0%, and where a storage elastic modulus of the magnetic toner at 40° C. is taken as E′(40) [Pa] and a storage elastic modulus of the magnetic toner at 85° C. is taken as E′(85) [Pa], the following formulas (1) and (2) are satisfied: E ′(85)≤5.5×10 9 (1) [ E ′(40)− E ′(85)]×100/ E ′(40)≥30 (2).
1. A magnetic toner, comprising:
a magnetic toner particle that includes a binder resin, a magnetic body, and a crystalline polyester; and
said toner having a dielectric loss tangent at 100 kHz of 1.0×10 −2 or more, wherein
in cross-sectional observation of the magnetic toner particle using a transmission electron microscope TEM, a variation coefficient CV3 of an occupied area ratio of the magnetic body when a cross section of the magnetic toner particle is divided by a square grid having a side of 0.8 μm is 30 to 80.0%, and
E′(85)≤5.5×10 9 and [E′(40)−E′(85)]×100/E′(40)≥30 when E′(40) [Pa] is a storage elastic modulus at 40° C. and E′(85) [Pa] is a storage elastic modulus at 85° C., the storage elastic moduli being obtained in a powder dynamic viscoelasticity measurement of the magnetic toner.
2. The magnetic toner according to claim 1 , wherein an amount of the crystalline polyester in the magnetic toner is 15.0% by mass or less.
3. The magnetic toner according to claim 1 , wherein an average value of the occupied area ratio of the magnetic body is 10 to 40.0%.
4. The magnetic toner according to claim 1 , wherein a number average diameter of domains of the crystalline polyester present in a cross section of the magnetic toner particle observed with a transmission electron microscope is 50 to 500 nm.
5. The magnetic toner according to claim 1 , wherein the magnetic toner has an average circularity of 0.960 or more.
6. The magnetic toner according to claim 1 , wherein the crystalline polyester includes a monomer unit derived from an aliphatic diol having a carbon number of C2 to C12, and/or a monomer unit derived from an aliphatic dicarboxylic acid having a carbon number of C2 to C12.
7. The magnetic toner according to claim 1 , wherein E′(85)≤5.0×10 9 .
8. The magnetic toner according to claim 1 , wherein CV2/CV1≤1.00 when CV1(%) is a variation coefficient of a brightness dispersion value of the magnetic toner in a range from Dn−0.500 to Dn+0.500, CV2(%) is a variation coefficient of a brightness dispersion value of the magnetic toner in a range from Dn−1.500 to Dn−0.500, and Dn (μm) is a number average particle diameter of the magnetic toner, and
an average brightness at the Dn of the magnetic toner is 30.0 to 60.0.
9. The magnetic toner according to claim 1 , wherein the binder resin includes an amorphous polyester.