Systems and methods for platinum nanocatalyst synthesis via continuous flow reactor
A method for synthesis of platinum nanoparticles by continuous flow using large flow segments. The nanoparticles are monodispersed and can undergo acid leaching to form platinum catalyst, such as PtNi or PtCo catalyst material.
1. A method of synthesizing Pt nanoparticle catalyst comprising the steps of:
forming, at an initial temperature of 18-28° C., a reaction mixture comprising a metal precursor comprising nickel acetate tetrahydrate, a reducing agent comprising 1,2-tetradecanediol, and a surfactant comprising one part oleic acid to two parts oleylamine, a platinum precursor comprising platinum acetylacetonate, and a polar solvent;
heating the reaction mixture at 110° C. for two hours, removing water;
injecting a segment of reaction mixture into a continuous flow reactor at a temperature of at least 190° C. for 5 minutes to 1 hour, forming a PtNi nanoparticle solution, the segment having a segment length of at least 3 mm;
isolating PtNi/substrate nanoparticles by:
sonicating the PtNi nanoparticle solution with substrate in chloroform solution,
adding hexane to the sonicated chloroform solution,
precipitating PtNi/substrate nanoparticles, and
collecting the PtNi/substrate nanoparticles by filtration;
annealing the PtNi/substrate nanoparticles in air at a first annealing temperature, removing surfactant from the PtNi/substrate nanoparticles;
acid leaching the PtNi/substrate nanoparticles by:
sonicating the collected PtNi/substrate nanoparticles in water,
mixing an acid with the sonicated PtNi/substrate sonicated in water for 60 minutes to form leached PtNi/substrate nanoparticles, and
collecting the leached PtNi/substrate nanoparticles by filtration; and
annealing the leached PtNi/substrate nanoparticles at a second annealing temperature, forming a Pt-skin on the PtNi/substrate nanoparticles.
2. The method of claim 1 , wherein the initial temperature is 20-24° C.
3. The method of claim 2 , wherein the segment length is at least 10 mm.
4. The method of claim 2 wherein the segment length is 5-10 mm.
5. The method of claim 4 , wherein the continuous flow reactor has a reactor tube diameter of 2-5 mm.
6. The method of claim 1 , wherein the polar solvent comprises dipehenyl ether and 1,2-dichlorobenzene.
7. The method of claim 1 , wherein the substrate is carbon.
8. The method of claim 1 , wherein the acid is HClO4.
9. The method of claim 1 , wherein annealing the leached PtNi/substrate nanoparticles at the second annealing temperature, forming the Pt-skin on the PtNi/substrate nanoparticles, comprises heating the leached PtNi/substrate nanoparticles at 400° C. for 1 hour under flow of 3% H 2 /Ar gas.
10. A method of forming platinum containing nanoparticles comprising:
forming, at an initial temperature of 18-28° C., a reaction mixture comprising a nickel precursor comprising nickel acetate tetrahydrate, a reducing agent comprising 1,2-tetradecanediol, a surfactant comprising one part oleic acid to two parts oleylamine, a platinum precursor comprising platinum acetylacetonate, and a polar solvent comprising 1,2-dichlorobenzene and diphenyl ether, wherein the reaction mixture comprises a ratio of 1.336 g nickel acetate tetrahydrate to 1.04 g platinum acetylacetonate to 0.68 g 1,2-tetradecanediol to 8 mL oleylamine to 4 mL oleic acid to 24 mL 1,2-dichlorobenzene, to 160 mL diphenyl ether; and
injecting a segment of reaction mixture into a continuous flow reactor at a temperature of at least 190° C. for 5 minutes to 1 hour, forming a platinum containing nanoparticle solution, the segment having a segment length of at least 3 mm.
11. The method of claim 10 , wherein the initial temperature is 20-24° C.
12. The method of claim 10 , wherein the segment length is at least 10 mm.
13. The method of claim 10 wherein the segment length is 5-10 mm.
14. The method of claim 13 , wherein the continuous flow reactor has a reactor tube diameter of 2-5 mm.
15. The method of claim 6 , wherein the reaction mixture comprises a ratio of 1.336 g nickel acetate tetrahydrate to 1.04 g platinum acetylacetonate to 0.68 g 1,2-tetradecanediol to 8 mL oleylamine to 4 mL oleic acid to 24 mL 1,2-dichlorobenzene, to 160 mL diphenyl ether.
16. A method of synthesizing Pt nanoparticle catalyst comprising the steps of:
forming, at an initial temperature of 18-28° C., a reaction mixture comprising a metal precursor comprising nickel acetate tetrahydrate, a reducing agent comprising 1,2-tetradecanediol, and a surfactant comprising one part oleic acid to two parts oleylamine, a platinum precursor comprising platinum acetylacetonate, and a polar solvent;
heating the reaction mixture at 110° C. for two hours, removing water;
injecting a segment of reaction mixture into a continuous flow reactor at a temperature of at least 190° C. for 5 minutes to 1 hour, forming a PtNi nanoparticle solution, the segment having a segment length of at least 3 mm;
isolating PtNi/substrate nanoparticles by:
sonicating the PtNi nanoparticle solution with substrate in chloroform solution,
adding hexane to the sonicated chloroform solution,
precipitating PtNi/substrate nanoparticles, and
collecting the PtNi/substrate nanoparticles by filtration;
annealing the PtNi/substrate nanoparticles in air at a first annealing temperature, removing surfactant from the PtNi/substrate nanoparticles;
acid leaching the PtNi/substrate nanoparticles by:
sonicating the collected PtNi/substrate nanoparticles in water,
mixing an acid with the sonicated PtNi/substrate sonicated in water for 60 minutes to form leached PtNi/substrate nanoparticles, and
collecting the leached PtNi/substrate nanoparticles by filtration; and
annealing the leached PtNi/substrate nanoparticles at a second annealing temperature, forming a Pt-skin on the PtNi/substrate nanoparticles;
wherein annealing the PtNi/substrate nanoparticles in air at the first annealing temperature, removing surfactant from the PtNi/substrate nanoparticles, comprises heating the PtNi/substrate nanoparticles at 185° C. for 20 hours.