Use of MGO, ZNO, and rare earth oxides for making improved low dielectric fibers with improved low thermal expansion coefficient for high boron aluminosilicate compositions
New glass compositions and applications thereof are disclosed. A glass composition as described herein can include 50 to 55 weight percent SiO 2 , 17 to 26 weight percent B 2 O 3 , 13 to 19 weight percent Al 2 O 3 , 0 to 8.5 weight percent MgO, 0 to 7.5 weight percent ZnO, 0 to 6 weight percent CaO, 0 to 1.5 weight percent Li 2 O, 0 to 1.5 weight percent F 2 , 0 to 1 weight percent Na 2 O, 0 to 1 weight percent Fe 2 O 3 , 0 to 1 weight percent TiO 2 , and 0 to 8 weight percent of other constituents. Also described herein are glass fibers formed from such compositions, composites, and articles of manufacture comprising the glass compositions and/or glass fibers.
1. A glass composition suitable for fiber forming comprising:
SiO 2 in an amount from 50 to 55 weight percent;
B 2 O 3 in an amount from 18 to 25 weight percent;
Al 2 O 3 in an amount from 13 to 19 weight percent;
MgO in an amount from 4.18 to 8.5 weight percent;
ZnO in an amount from 3.58 to 7.5 weight percent;
CaO in an amount from 0 to 4 weight percent;
Li 2 O in an amount from 0 to 1 weight percent;
F 2 in an amount from 0 to 1.5 weight percent;
Na 2 O in an amount from 0 to 1 weight percent;
Fe 2 O 3 in an amount from 0 to 0.6 weight percent;
TiO 2 in an amount from 0 to 1 weight percent; and
one or more rare earth oxides (RE 2 O 3 ) in an amount from 0 to 8 weight percent total,
wherein the composition is substantially free from SrO .
2. The composition of claim 1 , wherein the SiO 2 content is from 51 to 54 weight percent.
3. The composition of claim 1 , wherein the B 2 O 3 content is from 19 to 24 weight percent.
4. The composition of claim 1 , wherein the Al 2 O 3 content is from 14 to 18 weight percent.
5. The composition of claim 1 , wherein the ZnO content is from greater than 0 to 5 weight percent.
6. The composition of claim 1 , wherein the Na 2 O content is from greater than 0 to 0.5 weight percent.
7. The composition of claim 1 , wherein the Fe 2 O 3 content is from greater than 0 to 0.5 weight percent.
8. The composition of claim 1 , wherein the TiO 2 content is from greater than 0 to 0.6 weight percent.
9. The composition of claim 1 , wherein the glass composition comprises one or more rare earth oxides in an amount greater than 0.01 weight percent.
10. The composition of claim 1 , wherein the one or more rare earth oxides comprise at least one of La 2 O 3 , CeO 2 , Y 2 O 3 and Sc 2 O 3 .
11. The composition of claim 1 , wherein the Al 2 O 3 +MgO content is from 17.18 to 26.5 weight percent.
12. The composition of claim 1 , wherein the Al 2 O 3 +ZnO content is from 16.58 to 22 weight percent.
13. The composition of claim 1 , wherein the total Na 2 O+Li 2 O content is 1.5 weight percent or less.
14. The composition of claim 1 , wherein the total Al 2 O 3 +SiO 2 content is 65 to 74 weight percent.
15. The composition of claim 1 , wherein the total SiO 2 +B 2 O 3 content is 70 to 79.24 weight percent.
16. The composition of claim 1 , wherein the composition is substantially free from BaO.
17. A fiber formed from a composition of claim 1 .
18. An article of manufacture comprising a fiber of claim 17 .
19. The article of manufacture of claim 18 , wherein the article is a printed circuit board.
20. A glass composition suitable for fiber forming comprising:
SiO 2 in an amount from 50 to 55 weight percent;
B 2 O 3 in an amount from 17 to 26 weight percent;
Al 2 O 3 in an amount from 13 to 19 weight percent;
MgO in an amount from 6 to 8.5 weight percent;
ZnO in an amount from greater than 0 to 7.5 weight percent;
CaO in an amount from 0 to 2 weight percent;
Li 2 O in an amount from 0 to 1 weight percent;
F 2 in an amount from 0 to 1.5 weight percent;
Na 2 O in an amount from 0 to 1 weight percent;
Fe 2 O 3 in an amount from 0 to 1 weight percent;
TiO 2 in an amount from 0 to 1 weight percent; and
one or more rare earth oxides (RE 2 O 3 ) in an amount from 0 to 8 weight percent total,
wherein the composition is substantially free from SrO.
21. The composition of claim 20 , wherein the Al 2 O 3 content is from 14 to 18 weight percent.
22. The composition of claim 20 , wherein the Fe 2 O 3 content is from greater than 0 to 0.5 weight percent.
23. The composition of claim 20 , wherein the total Na 2 O+Li 2 O content is 0.1 weight percent or less.
24. The composition of claim 20 , wherein the total Al 2 O 3 +SiO 2 content is 65 to 74 weight percent.
25. The composition of claim 20 , wherein the total SiO 2 +B 2 O 3 content is 70 to 81 weight percent.
26. The composition of claim 20 , wherein the composition is substantially free from BaO.
27. A fiber formed from the composition of claim 20 .
28. An article of manufacture comprising a fiber of claim 27 .