Photocatalytic composite material and preparation method and application thereof
The present invention provides a preparation method of a photocatalytic composite material, and relates to the field of catalyst technologies. The preparation method provided in the present invention includes the following steps: (1) subjecting plant leaves to soaking pretreatment to obtain template biomass; (2) mixing a molybdenum source-sulfur source aqueous solution with the template biomass obtained in step (1) and conducting impregnation to obtain a composite material precursor; and (3) calcining the composite material precursor obtained in step (2) to obtain the photocatalytic composite material. The photocatalytic composite material in the present invention includes acicular molybdenum sulfide and biomass carbon, the acicular molybdenum sulfide is loaded to a surface of the flake carbon, the mass content of the biomass carbon is 70% to 90%, and the mass content of the molybdenum sulfide is 10% to 30%. Performance of photocatalytic hydrogen production of the photocatalytic composite material in the present invention is better than that of a pure molybdenum sulfide material and has excellent photocorrosion resistance, and hydrogen production efficiency is reduced by only approximately 10% after three cycles.
1. A preparation method of a photocatalytic composite material, comprising the following steps:
(1) subjecting plant leaves to soaking pretreatment to obtain template biomass;
(2) impregnating, in a molybdenum source-sulfur source aqueous solution, the template biomass obtained in step (1) to obtain a composite material precursor; and
(3) calcining the composite material precursor prepared in step (2) to obtain the photocatalytic composite material;
wherein a concentration of a molybdenum source in the molybdenum source-sulfur source aqueous solution is 0.05 mol/L to 1 mol/L.
2. The preparation method according to claim 1 , wherein the plant leaves comprise Sinaraundinaria nitida leaves, salix leaves, Indocalamus leaves, Phyllostachys sulphurea leaves, or Phyllostachys nigra leaves.
3. A photocatalytic composite material obtained by using the preparation method according to claim 2 , wherein the photocatalytic composite material comprises acicular molybdenum sulfide and biomass carbon, the acicular molybdenum sulfide is loaded to a surface of a flake carbon, the mass content of the biomass carbon is 70% to 90%, and the mass content of the molybdenum sulfide is 10% to 30%.
4. An application of the photocatalytic composite material according to claim 3 in water decomposition for hydrogen production.
5. The preparation method according to claim 1 , wherein a concentration of a sulfur source in the molybdenum source-sulfur source aqueous solution is 0.05 mol/L to 1 mol/L.
6. A photocatalytic composite material obtained by using the preparation method according to claim 5 , wherein the photocatalytic composite material comprises acicular molybdenum sulfide and biomass carbon, the acicular molybdenum sulfide is loaded to a surface of a flake carbon, the mass content of the biomass carbon is 70% to 90%, and the mass content of the molybdenum sulfide is 10% to 30%.
7. The preparation method according to claim 1 , wherein a ratio of a volume of the molybdenum source-sulfur source aqueous solution to a mass of the template biomass is (1-3) L: 100 g.
8. A photocatalytic composite material obtained by using the preparation method according to claim 7 , wherein the photocatalytic composite material comprises acicular molybdenum sulfide and biomass carbon, the acicular molybdenum sulfide is loaded to a surface of a flake carbon, the mass content of the biomass carbon is 70% to 90%, and the mass content of the molybdenum sulfide is 10% to 30%.
9. The preparation method according to claim 1 , wherein the calcination time is 120 min to 158 min.
10. A photocatalytic composite material obtained by using the preparation method according to claim 9 , wherein the photocatalytic composite material comprises acicular molybdenum sulfide and biomass carbon, the acicular molybdenum sulfide is loaded to a surface of a flake carbon, the mass content of the biomass carbon is 70% to 90%, and the mass content of the molybdenum sulfide is 10% to 30%.
11. A photocatalytic composite material obtained by using the preparation method according to claim 1 , wherein the photocatalytic composite material comprises acicular molybdenum sulfide and biomass carbon, the acicular molybdenum sulfide is loaded to a surface of a flake carbon, the mass content of the biomass carbon is 70% to 90%, and the mass content of the molybdenum sulfide is 10% to 30%.
12. An application of the photocatalytic composite material according to claim 11 in water decomposition for hydrogen production.
13. A preparation method of a photocatalytic composite material, comprising the following steps:
(1) subjecting plant leaves to soaking pretreatment to obtain template biomass;
(2) impregnating, in a molybdenum source-sulfur source aqueous solution, the template biomass obtained in step (1) to obtain a composite material precursor; and
(3) calcining the composite material precursor prepared in step (2) to obtain the photocatalytic composite material,
wherein an impregnation time is 48 h to 72 h.
14. A photocatalytic composite material obtained by using the preparation method according to claim 13 , wherein the photocatalytic composite material comprises acicular molybdenum sulfide and biomass carbon, the acicular molybdenum sulfide is loaded to a surface of a flake carbon, the mass content of the biomass carbon is 70% to 90%, and the mass content of the molybdenum sulfide is 10% to 30%.
15. A preparation method of a photocatalytic composite material, comprising the following steps:
(1) subjecting plant leaves to soaking pretreatment to obtain template biomass;
(2) impregnating, in a molybdenum source-sulfur source aqueous solution, the template biomass obtained in step (1) to obtain a composite material precursor; and
(3) calcining the composite material precursor prepared in step (2) to obtain the photocatalytic composite material,
wherein calcination temperature is 450° C. to 700° C.
16. The preparation method according to claim 15 , wherein the calcination time is 120 min to 158 min.
17. A photocatalytic composite material obtained by using the preparation method according to claim 16 , wherein the photocatalytic composite material comprises acicular molybdenum sulfide and biomass carbon, the acicular molybdenum sulfide is loaded to a surface of a flake carbon, the mass content of the biomass carbon is 70% to 90%, and the mass content of the molybdenum sulfide is 10% to 30%.
18. A photocatalytic composite material obtained by using the preparation method according to claim 15 , wherein the photocatalytic composite material comprises acicular molybdenum sulfide and biomass carbon, the acicular molybdenum sulfide is loaded to a surface of a flake carbon, the mass content of the biomass carbon is 70% to 90%, and the mass content of the molybdenum sulfide is 10% to 30%.