Recyclable, easily tearable packaging laminate having a good barrier effect and method for production thereof
A recyclable, easily tearable packaging laminate having a good barrier effect, including a first laminate layer and a second laminate layer. The the first laminate layer is a co-extruded, in the machine direction stretched composite consisting of a substrate layer having a high HDPE content of at least 60% by volume, a bonding layer and a barrier layer consisting of a barrier polymer, preferably polyamide or ethylene vinyl alcohol copolymer, having a maximum thickness of 20% of the overall thickness of the first laminate layer. The bonding layer is arranged between the substrate layer and the barrier layer and the first laminate layer is connected on the barrier layer thereof to the second laminate layer.
1 . A packaging laminate comprising
a first laminate and a second laminate,
the second laminate having a thickness between 20 μm and 200 μm and having a polyethylene content of at least 80% by volume,
the first laminate having been formed by coextruding a substrate layer with a HDPE content of at least 60% by volume, a bonding layer, and a barrier layer,
the thickness of the first laminate being between 10 μm and 40 μm,
the thickness of the substrate layer being between 5 μm and 35 μm,
the thickness of the bonding layer being between 1 μm and 5 μm,
the barrier layer having polyamide and/or ethylene-vinyl alcohol copolymer and having a thickness of at most 20% of the total thickness of the first laminate,
the bonding layer being arranged between the substrate layer and the barrier layer,
the first laminate being stretched in machine direction only,
the first laminate is bonded to the second laminate via its barrier layer after the first laminate is stretched, and
wherein said packaging laminate is tearable in both the machine direction and a transverse direction perpendicular to the machine direction.
2 . The packaging laminate according to claim 1 , wherein the barrier layer of the first laminate is printed and/or metallized and/or coated.
3 . The packaging laminate according to claim 1 , wherein the first laminate is bonded on its substrate layer to a further single-layer or multi-layer laminate layer having a polyethylene content of at least 80% by volume.
4 . The packaging laminate according to claim 3 , wherein at least one layer of the further laminate layer is printed and/or metallized and/or coated.
5 . The packaging laminate according to claim 3 , wherein the further laminate layer is stretched in machine direction and formed by co-extruding a substrate layer with a HDPE content of at least 60% by volume, a barrier layer having a barrier polymer, and a bonding layer arranged in between, wherein the substrate layer of the first laminate is bonded to the barrier layer of the further laminate layer.
6 . The packaging laminate according to claim 1 , wherein the second laminate is stretched in machine direction and is co-extruded with a substrate layer having a HDPE content of at least 60% by volume, a bonding layer, a barrier layer having a barrier polymer and having a maximum thickness of 20% of the total thickness of the second laminate, and a sealing layer, wherein the bonding layer of the second laminate is between the substrate layer and the barrier layer of the second laminate, and the sealing layer is arranged on the substrate layer, wherein the barrier layer of the second laminate is bonded to the barrier layer of the first laminate.
7 . The packaging laminate according to claim 1 , wherein the substrate layer of the first laminate has a HDPE content of at least 70% by volume.
8 . The packaging laminate according to claim 6 , wherein the substrate layer of the second laminate has a HDPE content of at least 70% by volume.
9 . The packaging laminate according to claim 5 , wherein the barrier polymer of the further laminate layer comprises a polyamide and/or an ethylene-vinyl alcohol copolymer.
10 . The packaging laminate according to claim 6 , wherein the barrier polymer of the second laminate comprises a polyamide and/or an ethylene-vinyl alcohol copolymer.
11 . A packaging laminate, comprising:
a composite comprising the packaging laminate of claim 1 ; and
a laminate layer bonded to the barrier layer or the substrate layer of the composite.
12 . The packaging laminate according to claim 11 , wherein the laminate layer comprises a multi-layer laminate.
13 . The packaging laminate according to claim 11 , wherein the laminate layer is a single-layer.
14 . The packaging laminate according to claim 1 , wherein the second laminate comprises a multi-layer laminate.
15 . The packaging laminate according to claim 1 , wherein the second laminate is a single-layer.
16 . The packaging laminate according to claim 1 , wherein:
the first laminate is coextruded with only the substrate layer, bonding layer, and barrier layer, and with no other layer.