Surface-coated cutting tool
A surface-coated cutting tool includes a substrate and a coating film that coats the substrate, wherein the coating film includes a WC 1-x layer composed of a compound represented by WC 1-x , where x is more than or equal to 0.54 and less than or equal to 0.58, and the compound represented by WC 1-x includes a hexagonal crystal structure.
1. A surface-coated cutting tool comprising a substrate and a coating film that coats the substrate, wherein
the coating film includes a WC 1-x layer composed of a compound represented by WC 1-x , where x is more than or equal to 0.54 and less than or equal to 0.58, and
the compound represented by WC 1-x includes a hexagonal crystal structure.
2. The surface-coated cutting tool according to claim 1 , wherein the WC 1-x layer is in contact with the substrate.
3. The surface-coated cutting tool according to claim 1 , wherein the WC 1-x , layer includes no free carbon.
4. The surface-coated cutting tool according to claim 1 , wherein the WC 1-x , layer has a film hardness of more than or equal to 3700 mgf/μm 2 and less than or equal to 4500 mgf/μm 2 .
5. The surface-coated cutting tool according to claim 1 , wherein
the coating film further includes a hard coating layer formed on the WC 1-x layer,
the hard coating layer at least includes a first unit layer having a composition different from a composition of the WC 1-x layer, and
the first unit layer is composed of at least one element selected from a group consisting of a group 4 element, a group 5 element, a group 6 element in a periodic table, Al, and Si, or is composed of a compound composed of at least one of the elements and at least one element selected from a group consisting of carbon, nitrogen, oxygen and boron.
6. The surface-coated cutting tool according to claim 5 , wherein the first unit layer has a thickness of more than or equal to 0.1 μm and less than or equal to 10 μm.
7. The surface-coated cutting tool according to claim 5 , wherein
the hard coating layer further includes a second unit layer having a composition different from compositions of the WC 1-x layer and the first unit layer,
the second unit layer is composed of at least one element selected from a group consisting of a group 4 element, a group 5 element, a group 6 element in the periodic table, Al, and Si, or is composed of a compound composed of at least one of the elements and at least one element selected from a group consisting of carbon, nitrogen, oxygen and boron, and
one or a plurality of the first unit layers and one or a plurality of the second unit layers are layered alternately on each other to form a multilayer structure.
8. The surface-coated cutting tool according to claim 7 , wherein the first unit layer has a thickness of more than or equal to 1 nm and less than or equal to 100 nm, and the second unit layer has a thickness of more than or equal to 1 nm and less than or equal to 100 nm.
9. The surface-coated cutting tool according to claim 1 , wherein the coating film has a thickness of more than or equal to 0.1 μm and less than or equal to 10 μm.
10. The surface-coated cutting tool according to claim 1 , wherein the substrate includes at least one selected from a group consisting of a cemented carbide, a cermet, a high-speed steel, a ceramic, a cBN sintered material, and a diamond sintered material.