Antimicrobial polymer composition
A polymer composition comprising an antimicrobial material for inhibiting the growth of microorganisms in close proximity to said polymer composition. The polymer composition comprises: (a) a polymeric substrate comprising a first polymer and a second polymer, and (b) an antimicrobial material comprising coniferous resin acid(s) dispersed in the polymeric substrate. The water contact angle of the first polymer is not more than 80°.
1. A polymer composition consisting of:
(a) a polymeric substrate consisting of a first polymer and a second polymer,
(b) an antimicrobial material in an amount of 5 wt-% to 15 wt-% of the polymer composition, the antimicrobial material consisting of coniferous resin acid(s) dispersed in the polymeric substrate,
wherein the water contact angle of the first polymer is not more than 80° to allow resin acids to diffuse from the polymer composition into a microorganism-containing aqueous phase,
wherein the first polymer is selected from a group consisting of (a) polyamide, (b) polyethylene-polyether-copolymer, polyethylene block amide, or polyether-polyamide block copolymer, or mixtures of two or more of the above mentioned polymers (a) and (b),
wherein the second polymer is selected from a group consisting of (i) polyolefin, (ii) styrene copolymer, (iii) polyester, or (iv) thermoplastic elastomer (TPE), or mixtures of two or more of the above mentioned polymers (i), (ii), (iii) and (iv), and
wherein the amount of the first polymer is 10 wt-% to 50 wt-% of the polymeric substrate, and the amount of the second polymer is 50 wt-% to 90 wt-% of the polymeric substrate.
2. The polymer composition of claim 1 , wherein the amount of the first polymer is 10 wt-% to 45 wt-% of the polymeric substrate, and the amount of the second polymer is 55 wt-% to 90 wt-% of the polymeric substrate.
3. The polymer composition of claim 1 , wherein the amount of high density polyethylene (HDPE) in the polymeric substrate is 90 wt-%.
4. The polymer composition of claim 1 , wherein the polymeric substrate consists of 45 wt-% of polyamide 6 (PA6) and 55 wt-% of polyolefins.
5. The polymer composition of claim 1 , wherein the antimicrobial material consists of a resin acid fraction which is substantially free from volatile terpenes.
6. The polymer composition of claim 1 , wherein the content of coniferous resin acid(s) in the antimicrobial material is in the range of 5 wt-% to 98 wt-%.
7. The polymer composition of claim 1 , wherein the water contact angle of the first polymer is not more than 75°.
8. The polymer composition of claim 1 , wherein the water contact angle of the first polymer is not more than 70°.
9. The polymer composition of claim 1 , wherein the polyamide is polyamide 6 (PA6).
10. The polymer composition of claim 1 , wherein the polyolefin is selected from HDPE, polypropylene (PP) and a mixture thereof.
11. The polymer composition of claim 1 , wherein the styrene copolymer is acrylonitrile butadiene styrene (ABS).
12. The polymer composition of claim 1 , wherein the polyester is selected from polyethylene terephthalate (PET), polybutylene terephthalate (PBT) and a mixture thereof.
13. The polymer composition of claim 1 , wherein the amount of the first polymer is 10 wt-% of the polymeric substrate.
14. The polymer composition of claim 1 , wherein the amount of the second polymer component is 55 wt-% to 70 wt-%.
15. The polymer composition of claim 1 , wherein the amount of the antimicrobial material is about 10 wt-% of the composition.
16. The polymer composition of claim 1 , wherein the content of coniferous resin acid(s) in the antimicrobial material is in the range of 70 wt-% to 96 wt-%.
17. The polymer composition of claim 1 , wherein the content of coniferous resin acid(s) in the antimicrobial material is in the range of 85 wt-% to 95 wt-%.
18. The polymer composition of claim 1 , wherein the first polymer is not water-soluble.
19. The polymer composition of claim 1 , wherein the first polymer and the second polymer are co-kneaded into the polymeric substrate.
20. A method for preparing the polymer composition of claim 1 , the method comprising:
providing the first and the second polymer,
providing the antimicrobial material consisting of the coniferous resin acid(s),
optionally drying the first and second polymers, and
dispersing the antimicrobial material into the polymeric substrate.
21. A method of inhibiting the growth of microorganisms in an environment by treating a surface of the environment with the composition of claim 1 .