Aluminum alloy foil, and method for producing aluminum alloy foil
An aluminum alloy foil has a composition containing 1.0% to 1.8% by mass of Fe, 0.10% to 0.20% by mass of Si, 0.005% to 0.05% by mass of Cu, and Mn regulated to be 0.01% by mass or less, with the balance consisting of Al and incidental impurities. With regard to crystal grains surrounded by high inclination angle grain boundaries which are grain boundaries having a misorientation of 15° or more in analysis of crystal orientation per unit area using electron backscatter diffraction, an average grain size of the crystal grains is 10 μm or less, and a maximum grain size of the crystal grains/the average grain size of the crystal grains ≤3.0. When a thickness of the foil is 30 μm, elongations in directions making 0°, 45° and 90° with respect to a rolling direction are each 25% or more respectively.
1. An aluminum alloy foil having a composition containing 1.0% by mass or more and 1.8% by mass or less of Fe, more than 0.10% by mass and 0.20% by mass or less of Si, 0.005% by mass or more and 0.05% by mass or less of Cu, Mn regulated to be 0.01% by mass or less, and the balance Al and incidental impurities,
wherein, with regard to crystal grains surrounded by high inclination angle grain boundaries which are grain boundaries having a misorientation of 15° or more in analysis of crystal orientation per unit area using electron backscatter diffraction, an average grain size of the crystal grains is 10 μm or less, and a maximum grain size of the crystal grains/the average grain size of the crystal grains ≤3.0, and when a thickness of the foil is 30 μm, elongations in directions making 0°, 45° and 90° with respect to a rolling direction are each 25% or more respectively.
2. The aluminum alloy foil according to claim 1 , wherein, as a texture, a Cu orientation density is 40 or less, and an R orientation density is 30 or less.
3. A method for producing the aluminum alloy foil according to claim 1 , comprising:
subjecting an ingot of an aluminum alloy having said composition to homogenization treatment comprising holding the ingot at 460° C. to 550° C. for 6 hours or more,
after the homogenization treatment, subjecting the ingot to hot rolling such that a rolling finishing temperature becomes 230° C. or more and less than 300° C., and
during cold rolling, performing intermediate annealing at 300° C. to 400° C., to achieve a cold rolling rate of 30% or more and 70% or less obtained from the start of the cold rolling to the intermediate annealing, and a final cold rolling rate of 97% or more obtained from the completion of the intermediate annealing to a time point at which a final thickness is achieved.
4. A method for producing the aluminum alloy foil according to claim 2 , comprising:
subjecting an ingot of an aluminum alloy having said composition to homogenization treatment comprising holding the ingot at 460° C. to 550° C. for 6 hours or more,
after the homogenization treatment, subjecting the ingot to hot rolling such that a rolling finishing temperature becomes 230° C. or more and less than 300° C., and
during cold rolling, performing intermediate annealing at 300° C. to 400° C., to achieve a cold rolling rate of 30% or more and 70% or less obtained from the start of the cold rolling to the intermediate annealing, and a final cold rolling rate of 97% or more obtained from the completion of the intermediate annealing to a time point at which a final thickness is achieved.