Carbon-coated silicon oxide/graphite composite particles, methods of making, and applications of the same
The present disclosure relates to novel particulate composite materials comprising a graphitic core particle associated with SiOx nanoparticles (0.2≤X≤1.8), and coated by a layer of non-graphitic carbon, e.g., pyrolytic carbon deposited by chemical vapor deposition (CVD). Also included are processes for making such particles as well as uses and downstream products for the novel composite material, in particular as an active material in negative electrodes in Li-ion batteries.
1. A particulate composite material comprising a nano- SiO X /graphite composite particle comprising a graphitic core particle associated with SiOx nanoparticles, wherein X is between 0.2 and 1.8, and wherein the nano-SiO x / graphite composite particle is coated by a layer of non-graphitic carbon;
wherein the non-graphitic carbon layer is pyrolytic carbon;
wherein the SiOx nanoparticles are characterized by a particle size distribution (PSD) with a D 50 of 15 to 100 nm; and
wherein the SiOx nanoparticles are associated with the surface of the graphitic core particle.
2. The composite material of claims 1 , wherein the pyrolytic carbon is deposited by chemical vapor deposition (CVD).
3. The composite material of claim 1 , wherein the graphitic core particle is either spherically-shaped natural graphite having an average aspect ratio between the shortest and longest axis of the spherically-shaped natural graphite core particles that is between about 0.4 and about 1.0, or synthetic graphite having an average aspect ratio that is between about 0.1 and about 0.6.
4. The composite material of claim 1 , wherein the composite material is further characterized by any one or more of the following parameters:
i) a thickness of the non-graphitic continuous coating layer of between about 5 to about 200 nm, or between about 10 and about;
ii) a particle size distribution (PSD) with a D 50 of about 15 to about 50 μm;
iii) a BET SSA of about 1 m 2 /g to about 15 m 2 /g;
iv) a crystallographic L c value of at least about 30 nm;
v) a Raman I D /I G ratio (R (I D /I G )) of larger than about 0.2 when measured with a laser having an excitation wavelength of 632.8 nm; and
vi) a particle size distribution (PSD) with a D 90 of less than about 60 μm.
5. The composite material of claim 1 , wherein the composite material is further characterized by any one or more of the following parameters:
i) an initial coulombic efficiency of at least 75%, when used as an active material in the negative electrode of a lithium ion battery; and
ii) a rate capability at 3C of at least 65%, when used as an active material in the negative electrode of a lithium ion battery.
6. A composition comprising the particulate composite material according to claim 1 , wherein the composition further comprises natural graphite, synthetic graphite, and/or graphitized mesocarbon beads.
7. A dispersion comprising the particulate composite material according to claim 1 in a liquid, wherein the liquid is water, an organic solvent, or mixtures thereof.
8. A negative electrode comprising the particulate composite material according to claim 1 as an active material.
9. A lithium ion battery comprising the negative electrode according to claim 8 .