Coated cutting tool, and method and system for manufacturing the same by chemical vapor deposition

1. A coated cutting tool comprising:

a substrate; and

a hard film coated on the substrate, wherein

the hard film comprises aggregates of columnar grains grown on the substrate along the thickness of the film,

the hard film comprises a complex nitride of Al and Cr, the nitride having an Al content of 60 atom % or more and 90 atom % or less, a Cr content of 10 atom % or more, and a total content of Al and Cr of 90 atom % or more relative to the total amount of metal and metalloid elements;

the complex nitride in the hard film primarily has an fcc structure, one of nine peaks assigned to crystal planes (111), (200), (220), (311), (222), (400), (331), (420), and (422) of the fcc structure exhibiting the highest intensity in X-ray diffractometry, and

the hard film has a ratio TC (311) of an X-ray diffraction intensity of 1.30 or more, wherein

the ratio TC (311) is determined by an expression:

TC (311)={1(311)/Io(311)}/[Z(1(hkl)/Io(hkl)}/8] wherein

I(hkl) is an observed X-ray diffraction intensity assigned to each crystal plane (hkl) of the complex nitride,

Io(hkl) is the standard X-ray diffraction intensity assigned to the corresponding crystal plane (hkl) of the aluminum nitride listed in File No. 00-025-1495 available from International Center for Diffraction Data (ICDD), Σ represents the sum of the observed X-ray diffraction intensities assigned to eight crystal planes (111), (200), (220), (311), (222), (400), (331), and (420).

2. The coated cutting tool according to claim 1 , wherein the ratio TC (311) of the X-ray diffraction intensity is 2.00 or more.

3. The coated cutting according to claim 1 , wherein the ratio TC (311) of the X-ray diffraction intensity is higher than the ratios TC (hkl) assigned to crystal planes (111), (200), (220), (311), (222), (400), (331), and (420).

4. The coated cutting tool according to claim 1 , wherein the ratios TC (420) and TC (200) of the X-ray diffraction intensities are each 1.00 .

5. The coated cutting tool according to claim 1 , wherein the hard film satisfies a ratio TB/TA of 0.050 or more in the X-ray diffractometry, wherein TA represents the total peak intensity assigned to the crystal planes of the fcc structure and TB represents the peak intensity assigned to the crystal plane (422).

6. The coated cutting tool according to claim 1 , wherein the columnar grains each have an average width of 0.1 μm or more and 2.0 μm or less at 0.5 μm from the surface of the hard film.

7. The coated cutting tool according to claim 1 , wherein the hard film comprises dispersed crystal grains in a micro structure observed by transmission electron microscopy, the crystal grains each having a monolayer structure with a relatively high Al content and a multilayer structure with a relatively low Al content.

8. The coated cutting tool according to claim 1 , further comprising an intermediate film between the substrate and the hard film.

9. The coated cutting tool according to claim 1 , further comprising an upper layer on the hard film.

10. The coated cutting according to claim 2 , wherein the ratio TC (311) of the X-ray diffraction intensity is higher than the ratios TC (hkl) assigned to crystal planes (111), (200), (220), (222), (400), (331), and (420).