Method and firing apparatus for manufacturing cathode active material for lithium ion secondary battery
A method for manufacturing a cathode active material for a lithium ion secondary battery comprises mixing lithium carbonate and a compound containing a metal element other than Li, and a firing step. The firing step includes at last two stages of controlling firing to different temperatures. The at least two stages include controlling a firing temperature to a lower temperature and controlling a firing temperature to a higher temperature. The firing is controlled is such that the former stage has a lower oxygen concentration in an atmosphere than the latter stage. The firing apparatus comprises at least two firing furnaces of controlling firing temperatures to different temperatures. The at least two firing furnaces include controlling a firing temperature to a lower temperature and controlling firing temperature to a higher temperature. The latter firing furnace has a gas outlet being in communication with the former firing furnace.
1. A method for manufacturing a cathode active material used for a lithium ion secondary battery and represented by the following formula (1), comprising:
a mixing step of mixing lithium carbonate and a compound containing a metal element shown in the following formula (1) other than Li; and
a firing step of producing a lithium composite compound represented by the following formula (1) by firing a precursor produced through the mixing step, wherein
the firing step includes at least one of a first stage of controlling a firing temperature to less than 720° C. and a second stage of controlling a firing temperature to 720° C. or more and less than 770° C.,
the firing step further includes a third stage of controlling a firing temperature to 770° C. or more,
the first stage is controlled to have an atmosphere having an oxygen concentration of from 45% to 75% both inclusive,
the second stage is controlled to have an atmosphere having an oxygen concentration of from 55% to 85% both inclusive,
the third stage is controlled to have an atmosphere having an oxygen concentration of from 80% to 100% both inclusive, and
the firing is performed while a gas discharged from the atmosphere of the third stage is introduced into at least one of the atmosphere of the first stage and the atmosphere of the second stage
Li 1+a M1O 2+α (1)
provided that (a) in the formula (1), M1 is a metal element other than Li and contains at least Ni and (b) a and a are numbers satisfying −0.1≤a≤0.2 and −0.2≤α≤0.2 respectively.
2. The method for manufacturing a cathode active material used for a lithium ion secondary battery according to claim 1 , wherein the discharged gas is introduced after a carbon dioxide concentration is reduced to 0.02% or less.
3. The method for manufacturing a cathode active material used for a lithium ion secondary battery according to claim 2 , wherein a carbon dioxide removal means is used to reduce the carbon dioxide concentration by removing carbon dioxide.
4. A method for manufacturing a cathode active material used for a lithium ion secondary battery and represented by the following formula (1), comprising:
a mixing step of mixing lithium carbonate and a compound containing a metal element shown in the following formula (1) other than Li; and
a firing step of producing a lithium composite compound represented by the following formula (1) by firing a precursor produced through the mixing step, wherein
the firing step includes a fourth stage of controlling a firing temperature to less than 720° C., a fifth stage of controlling a firing temperature to 720° C. or more and less than 770° C., and a sixth stage of controlling a firing temperature to 770° C. or more,
the fourth stage is controlled to have an atmosphere having an oxygen concentration of from 45% to 75% both inclusive,
the fifth stage is controlled to have an atmosphere having an oxygen concentration of from 55% to 85% both inclusive,
the sixth stage is controlled to have an atmosphere having an oxygen concentration of from 80% to 100% both inclusive, and
the firing is performed while gases discharged from the atmosphere of the fifth stage and discharged from the atmosphere of the sixth stage is introduced into the atmosphere of the fourth stage
Li 1+a M1O 2+α (1)
provided that (a) in the formula (1), M1 is a metal element other than Li and contains at least Ni and (b) a and a are numbers satisfying −0.1≤a≤0.2 and −0.2≤α≤0.2 respectively.
5. The method for manufacturing a cathode active material used for a lithium ion secondary battery according to claim 4 , wherein the discharged gas is introduced after a carbon dioxide concentration is reduced to 0.02% or less.
6. The method for manufacturing a cathode active material used for a lithium ion secondary battery according to claim 5 , wherein a carbon dioxide removal means is used to reduce the carbon dioxide concentration by removing carbon dioxide.
7. The method for manufacturing a cathode active material used for a lithium ion secondary battery according to claim 6 , wherein a carbon dioxide removal means is used to reduce the carbon dioxide concentration by removing carbon dioxide.