Aluminium alloy substrate for magnetic disk, method for fabricating the same, and magnetic disk composed of aluminium alloy substrate for magnetic disk
Provided is an aluminium alloy substrate for a magnetic disk, a method for fabricating the substrate, and a magnetic disk composed of the aluminium alloy substrate for a magnetic disk. The substrate contains an aluminium alloy composed of one or more elements selected from a group comprising 0.05 to 3.00 mass % (hereinafter abbreviated as “%”) of Fe, 0.05% to 3.00% of Mn, 0.05% to 18.00% of Si, 0.05% to 8.00% of Ni, 0.05% to 3.00% of Cr, and 0.05% to 3.00% of Zr, with a balance of Al and unavoidable impurities. The substrate has a Young modulus of 67 GPa or more in each of the 0° direction, 45° direction, and 90° direction relative to the rolling direction of the substrate.
1. An aluminium alloy substrate for a magnetic disk, the substrate comprising an aluminium alloy comprising:
one or more elements selected from a group consisting of 0.05 to 3.00 mass % of Fe, 0.05 to 3.00 mass % of Mn, 0.05 to 18.00 mass % of Si, 0.05 to 8.00 mass % of Ni, 0.05 to 3.00 mass % of Cr, and 0.05 to 3.00 mass % of Zr, and one or more elements selected from a group consisting of 0.003 to 8.000 mass % of Cu, 0.05 to 0.90 mass % of Mg and 0.005 to 8.000 mass % of Zn, with a balance of Al and unavoidable impurities, wherein
the substrate has a Young modulus of 67 GPa or more in each of a 0° direction, 45° direction, and 90° direction relative to a rolling direction of the substrate.
2. The aluminium alloy substrate for a magnetic disk according to any claim 1 , wherein the aluminium alloy further comprises one or more elements selected from a group consisting of Ti, B, and V at a total content of 0.005 to 0.500 mass %.
3. The aluminium alloy substrate for a magnetic disk according to claim 1 , wherein a product of a loss factor and a thickness (mm) of the substrate is 0.7×10 −3 mm or more in each of the 0° direction, 45° direction, and 90° direction relative to the rolling direction of the substrate.
4. A magnetic disk comprising:
the aluminium alloy substrate for a magnetic disk according to claim 1 ;
an electroless Ni—P plated layer on a surface of the substrate; and
a magnetic material layer on the plated layer.
5. A method of fabricating the aluminium alloy substrate for a magnetic disk according to claim 1 , the method comprising:
a semi-continuous casting step on casting the aluminium alloy to produce an ingot by a semi-continuous casting method;
a hot rolling step of hot rolling the ingot to produce a hot rolled plate;
a cold rolling step of cold rolling the hot rolled plate;
a disk blank punching step of punching the cold rolled plate to produce a disk blank having an annular shape;
a pressure annealing step of pressure annealing the disk blank; and
a cutting and grinding step of cutting and grinding the pressure annealed disk blank, wherein
in the cold rolling step, a difference in rotational speed between upper and lower rollers is 5% or less and a rolling speed is 1000 m/min or less.
6. A method of fabricating the aluminum alloy substrate for a magnetic disk according to claim 1 , the method comprising:
a continuous casting step of casting the aluminium alloy to produce a cast plate by a continuous casting method;
a cold rolling step of cold tolling the cast plate after continuous casting;
a disk blank punching step of punching the cold rolled plate to produce a disk blank having an annular shape;
a pressure annealing step of pressure annealing the disk blank; and
a cutting and grinding step of cutting and grinding the pressure annealed disk blank, wherein
in the cold rolling step, a difference in rotational speed between upper and lower rollers is 5% or less and a rolling speed is 1000 m/min or less.