Secondary battery pack with improved thermal management
The present invention relates to a novel secondary battery pack with improved thermal management useful for an all-electric vehicle (EV), a plug-in hybrid vehicle (PHEV), a hybrid vehicle (HEV), or battery packs used for other vehicles batteries, and more particularly, to the use of a specific material for thermally insulating a secondary battery pack and further minimizing the propagation of thermal runaway within a battery pack.
1. A process for preparation of a secondary battery pack comprising
at least one battery module casing 102 in which is disposed a plurality of battery cells 103 which are electrically connected to one another,
a silicone rubber syntactic foam comprising a silicone rubber binder and hollow glass beads, and said silicone rubber syntactic foam fills partially or fully the open space of said battery module casing 102 and/or covering partially or totally said battery cells 103 and/or covering partially or totally said module casing 102 , and
optionally a lid covering the battery module casing 102 ; and
wherein said silicone rubber syntactic foam is obtained by curing an addition curing type organopolysiloxane composition X, the process comprising
a) preparing at least one battery module casing 102 in which is disposed a plurality of battery cells 103 which are electrically connected to one another,
b) introducing into the said battery module casing 102 the addition curing type organopolysiloxane composition X,
c) filling completely or partially said battery module casing 102 , and
d) allowing the curing to occur so as to form a silicone rubber syntactic foam comprising a silicone rubber binder and hollow glass beads, and optionally
e) covering the battery module casing 102 with a lid
f) feeding into a base feed line a liquid silicone base MS1 comprising:
i) at least one organopolysiloxane A having at least two alkenyl groups bonded to silicon per molecule, said alkenyl groups each containing from 2 to 14 carbon atoms, preferably said alkenyl groups are chosen from the group consisting of vinyl, allyl, hexenyl, decenyl and tetradecenyl, and most preferably said alkenyl groups are vinyl groups,
ii) hollow glass beads D, and preferably hollow borosilicate glass microspheres D1,
iii) at least one silicon compound B having at least two and preferably at least three hydrogen atoms bonded to silicon per molecule, and
iv) optionally a cure rate controller G which slows the curing rate,
g) feeding into a catalyst feed line a catalyst master batch MC comprising:
i) at least one hydrosilylation catalyst C; and
ii) optionally, at least one organopolysiloxane A having at least two alkenyl groups bonded to silicon per molecule, said alkenyl groups each containing from 2 to 14 carbon atoms, preferably said alkenyl groups are chosen from the group consisting of vinyl, allyl, hexenyl, decenyl and tetradecenyl, and most preferably said alkenyl groups are vinyl groups;
h) feeding into an inhibitor feed line an inhibitor master batch MI comprising:
i) a cure rate controller G which slows the curing rate; and
ii) optionally, at least one organopolysiloxane A having at least two alkenyl groups bonded to silicon per molecule, said alkenyl groups each containing from 2 to 14 carbon atoms, preferably said alkenyl groups are chosen from the group consisting of vinyl, allyl, hexenyl, decenyl and tetradecenyl, and most preferably said alkenyl groups are vinyl groups; and
i) optionally feeding into an additive feed line an additive masterbatch MA comprising:
i) at least one additive H such as a pigment, a dye, clays, a surfactant, hydrogenated castor oil, wollastonite, aluminium trihydrate, magnesium hydroxide, halloysite, huntite, hydromagnesite, expandable graphite, zinc borate, mica or a fumed silica, and
ii) optionally at least one organopolysiloxane A having at least two alkenyl groups bonded to silicon per molecule, said alkenyl groups each containing from 2 to 14 carbon atoms, preferably said alkenyl groups are chosen from the group consisting of vinyl, allyl, hexenyl, decenyl and tetradecenyl, and most preferably said alkenyl groups are vinyl groups; and
j) directing said liquid silicone base MS1, said catalyst master batch MC and said inhibitor master batch MI and optionally said additive masterbatch MA into a tank to obtain the addition curing type organopolysiloxane composition X.
2. A process according to claim 1 wherein the preparation of the addition curing type organopolysiloxane composition X comprising the steps of:
a) feeding into a base feed line a liquid silicone base MS2 comprising:
i) at least one organopolysiloxane A having at least two alkenyl groups bonded to silicon per molecule, said alkenyl groups each containing from 2 to 14 carbon atoms, preferably said alkenyl groups are chosen from the group consisting of vinyl, allyl, hexenyl, decenyl and tetradecenyl, and most preferably said alkenyl groups are vinyl groups, and
ii) at least one silicon compound B having at least two and preferably at least three hydrogen atoms bonded to silicon per molecule,
iii) optionally a cure rate controller G which slows the curing rate,
b) feeding into a catalyst feed line a catalyst master batch MC comprising:
i) at least one hydrosilylation catalyst C; and
ii) optionally, at least one organopolysiloxane A having at least two alkenyl groups bonded to silicon per molecule, said alkenyl groups each containing from 2 to 14 carbon atoms, preferably said alkenyl groups are chosen from the group consisting of vinyl, allyl, hexenyl, decenyl and tetradecenyl, and most preferably said alkenyl groups are vinyl groups;
c) feeding into an inhibitor feed line an inhibitor master batch MI comprising:
i) a cure rate controller G which slows the curing rate; and
ii) optionally, at least one organopolysiloxane A having at least two alkenyl groups bonded to silicon per molecule, said alkenyl groups each containing from 2 to 14 carbon atoms, preferably said alkenyl groups are chosen from the group consisting of vinyl, allyl, hexenyl, decenyl and tetradecenyl, and most preferably said alkenyl groups are vinyl groups; and
d) optionally feeding into an additive feed line an additive masterbatch MA comprising:
i) at least one additive H such as a pigment, a dye, days, a surfactant, hydrogenated castor oil, wollastonite, aluminium trihydrate, magnesium hydroxide, halloysite, huntite hydromagnesite, expandable graphite, zinc borate, mica or a fumed silica, and
ii) optionally at least one organopolysiloxane A having at least two alkenyl groups bonded to silicon per molecule, said alkenyl groups each containing from 2 to 14 carbon atoms, preferably said alkenyl groups are chosen from the group consisting of vinyl, allyl, hexenyl, decenyl and tetradecenyl, and most preferably said alkenyl groups are vinyl groups;
e) directing said liquid silicone base MS2, said catalyst master batch MC and said inhibitor master batch MI and optionally said additive masterbatch MA into a stirring tank; and
f) operating said stirring tank, thereby mixing said liquid silicone base MS1, said catalyst master batch MC and said inhibitor master batch MI and optionally said additive masterbatch MA preferably by using a high flow, low-shear mixer, and
g) adding hollow glass beads D and preferably hollow borosilicate glass microspheres D1 into said stirring tank, preferably by means using gravity discharge or screw feeder to obtain the addition curing type organopolysiloxane composition X.