Adhesives and methods of making the same
Embodiments of this invention relate to adhesives, and more particularly to biomimetic heteropolymer adhesive compositions. Certain embodiments relate to biomimetic terpolymer adhesive compositions including dopamine methacrylamide, 3,4-dihydroxyphenylalanine, or 3,4-dihydroxystyrene, mimicking moieties found in marine mussel adhesive proteins. In some embodiments, elastic moduli of the adhesives are preferably selected to match the elastic moduli of the substrates to minimize stress concentrations, to increase the ductility of the adhesive-substrate system, or both.
1. A method of adhering, the method comprising:
selecting a pair of substrates to be adhered;
determining an elastic modulus of each substrate; and
adhering the substrates using a heteropolymer adhesive including a plurality of cross-linking monomers, a plurality of softening monomers, and a plurality of stiffening monomers;
wherein the cross-linking monomers are one of dopamine methacrylamide, 3,4-dihydroxyphenylalanine, and 3,4-dihydroxystyrene;
wherein the softening monomers include a poly(ethylene glycol) moiety;
wherein the stiffening monomers are one of methyl methacrylate and styrene;
wherein the plurality of cross-linking monomers, the plurality of softening monomers, and the plurality of stiffening monomers are present in proportions resulting in an elastic modulus of the heteropolymer adhesive less than 25× greater than the elastic modulus of at least one of the pair of substrates, and less than 25× lower than the elastic modulus of at least one of the pair of substrates.
2. The method of claim 1 , wherein the stiffening monomers are methyl methacrylate.
3. The method of claim 1 , wherein the softening monomers are poly(ethylene glycol) methyl ether methacrylate.
4. The method of claim 1 , wherein the cross-linking monomers are present in a proportion of about 10% to about 50% by mole percentage.
5. The method of claim 4 , wherein the cross-linking monomers are present in a proportion of about 20% to about 40% by mole percentage.
6. The method of claim 1 , wherein the plurality of cross-linking monomers, the plurality of softening monomers, and the plurality of stiffening monomers are present in proportions resulting in an elastic modulus of the heteropolymer adhesive substantially equal to the elastic modulus of at least one of the pair of substrates.
7. The method of claim 1 , wherein the plurality of cross-linking monomers, the plurality of softening monomers, and the plurality of stiffening monomers are present in proportions resulting in an elastic modulus of the heteropolymer adhesive less than 10× greater than the elastic modulus of at least one of the pair of substrates, and less than 10× lower than the elastic modulus of at least one of the pair of substrates.