Effect pigments
Effect pigments based on Al 2 O 3 flakes with high weather resistance and less photoactivity and to their use thereof in paints, industrial coatings, automotive coatings, printing inks, cosmetic formulations. The effect pigments have a ratio of the amount by weight of Al 2 O 3 of the Al 2 O 3 flake and the amount by weight of the metal oxide(s) of the coating layer(s) in the range of from 27:73 to 83:17 based on the total weight of the effect pigment.
1. An effect pigment based on an Al 2 O 3 flake which comprises an Al 2 O 3 flake coated with one or more layers of a metal oxide and/or a metal oxide mixture:
wherein the ratio of the amount by weight of Al 2 O 3 of the Al 2 O 3 flake to the amount by weight of the metal oxide(s) of the coating layer(s) is in the range of from 27:73 to 83:17 based on the total weight of the effect pigment;
wherein one or more layers of a metal oxide and/or a metal oxide mixture comprise one or more layers of metal oxides selected of TiO 2 , Fe 2 O 3 , Fe 3 O 4 , SnO 2 , ZrO 2 or Cr 2 O 3 ;
wherein the thickness of each metal oxide and/or a metal oxide mixture layer on the Al 2 O 3 flakes is 20-400 nm with the exception of any SnO 2 layer, which has a layer thickness of 1-400 nm;
wherein the effect pigment contains on the surface a protective layer containing at least one rare earth metal oxide, at least one metal oxide that is silicon, aluminum or zirconium or mixtures thereof, and an organic compound, and
wherein the protective layer contains 0.2-2 wt. % of the at least one rare earth metal oxide, 0.2-2 wt. % of SiO2, 0.2-4 wt. % of Al2O3 and/or ZrO2 and 1-10 wt. % of the organic compound.
2. The effect pigment according to claim 1 wherein the Al 2 O 3 flake is coated on the surface with one or two metal oxide layers.
3. The effect pigment according to claim 1 , wherein the Al 2 O 3 flake is doped with TiO 2 , ZrO 2 , SiO 2 , SnO 2 , In 2 O 3 or ZnO or a combination thereof.
4. The effect pigment according to claim 3 , wherein the amount of doping is 0.01-5% by weight based on the Al 2 O 3 flake.
5. The effect pigment according to claim 1 , wherein the Al 2 O 3 flake is doped with TiO 2 or ZnO.
6. The effect pigment according to claim 1 , wherein the particle thickness of the Al 2 O 3 flake is in the range of 130-500 nm.
7. The effect pigment according to claim 1 , wherein the Al 2 O 3 flake has a standard deviation of thickness distribution of less than 80.
8. The effect pigment according to claim 1 , wherein the Al 2 O 3 flake is coated to provide the following layer sequence:
Al 2 O 3 flake+TiO 2
Al 2 O 3 flake+TiO 2 /Fe 2 O 3
Al 2 O 3 flake+Fe 2 O 3
Al 2 O 3 flake+Fe 3 O 4
Al 2 O 3 flake+TiO 2 +Fe 2 O 3
Al 2 O 3 flake+TiO 2 +Fe 3 O 4
Al 2 O 3 flake+TiO 2 +SiO 2 +TiO 2
Al 2 O 3 flake+TiO 2 +MgO/SiO 2 +TiO 2
Al 2 O 3 flake+Fe 2 O 3 +SiO 2 +TiO 2
Al 2 O 3 flake+TiO 2 /Fe 2 O 3 +SiO 2 +TiO 2
Al 2 O 3 flake+TiO 2 +SiO 2 +TiO 2 /Fe 2 O 3
Al 2 O 3 flake+TiO 2 /Fe 2 O 3 +SiO 2 +TiO 2 /Fe 2 O 3
Al 2 O 3 flake+TiO 2 +SiO 2
Al 2 O 3 flake+TiO 2 +SiO 2 /Al 2 O 3
Al 2 O 3 flake+TiO 2 +Al 2 O 3
Al 2 O 3 flake+SnO 2
Al 2 O 3 flake+SnO 2 +Fe 2 O 3
Al 2 O 3 flake+SnO 2 +TiO 2
Al 2 O 3 flake+ZrO 2
Al 2 O 3 flake+TiO 2 +Prussian Blue
Al 2 O 3 flake+TiO 2 +Carmine Red,
wherein a / mark indicates a mixed oxide.
9. The effect pigment according to claim 1 , wherein the Al 2 O 3 flake is coated with TiO 2 in the rutile or anatase modification.
10. The effect pigment according to claim 1 , wherein the Al 2 O 3 flake is coated with TiO 2 in the rutile modification.
11. The effect pigment according to claim 1 , wherein the organic compound is organic coupling agents, organofunctional silanes, amino compounds or organic phosphorus compounds.
12. The effect pigment according to claim 1 , wherein the rare earth metal oxide in the protective layer is cerium oxide.
13. The effect pigment according to claim 1 , wherein the amount of the rare earth metal oxide in the effect pigment is ≤1 wt. %.
14. The effect pigment according to claim 1 , wherein the protective layer has a thickness of 0.5-10 nm.
15. A formulation which comprises an effect pigment according to claim 1 which formulation is a formulation for: paints; coatings; automobile coatings; automotive finishing; industrial coatings; powder coatings; printing inks; security printing inks; plastics; ceramic materials; cosmetics; glasses; paper; paper coating; toners for electrophotographic printing processes; seeds; greenhouse sheeting or tarpaulins; thermally conductive, self-supporting, electrically insulating, flexible sheets for the insulation of machines or devices; an absorber in the laser marking of paper and plastics; an absorber in the laser welding of plastics; pigment pastes with water; organic and/or aqueous solvents; a pigment preparation; or a dry pigment preparation.
16. A formulation containing one or more effect pigments according to claim 1 in an amount of 0.01-95% by weight, based on the formulation as a whole.
17. A formulation containing one or more effect pigments according to claim 1 , which further comprises at least one component selected from the group consisting of: water, polyols, polar and nonpolar oils, fats, waxes, film formers, polymers, copolymers, surfactants, free-radical scavengers, antioxidants, stabilisers, odour enhancers, silicone oils, emulsifiers, solvents, preservatives, thickeners, rheological additives, fragrances, colorants, other effect pigments, UV absorbers, surface-active assistants, cosmetic active compounds, fillers, binders, pearlescent pigments, color pigments and organic dyes.
18. The effect pigment according to claim 1 , wherein the interference and/or masstone color of the effect pigment is silver, and the ratio of the amount by weight of Al 2 O 3 of the Al 2 O 3 flakes to the amount by weight of the metal oxide(s) of the coating layer(s) is in the range of from 60:40 to 80:20 based on the total weight of the effect pigment.
19. The effect pigment according to claim 1 , wherein the interference and/or masstone color of the effect pigment is blue, to the ratio of the amount by weight of Al 2 O 3 of the Al 2 O 3 flakes and the amount by weight of the metal oxide(s) of the coating layer(s) is in the range of from 35:65 to 60:40 based on the total weight of the effect pigment.
20. The effect pigment according to claim 1 , wherein the interference and/or masstone color of the effect pigment is red, to the ratio of the amount by weight of Al 2 O 3 of the Al 2 O 3 flakes and the amount by weight of the metal oxide(s) of the coating layer(s) is in the range of from 35:65 to 65:35 based on the total weight of the effect pigment.