Transmission belt
A power transmission belt is at least partially formed of a rubber composition. The rubber composition contains a rubber component, cellulose nanofibers, and carbon black. The amount of the cellulose nanofibers to be added is from 0.1 parts by mass to 20 parts by mass, relative to 100 parts by mass of the rubber component. The amount of the carbon black to be added is from 5 parts by mass to 80 parts by mass, relative to 100 parts by mass of the rubber component. The sum of the amount of the carbon black to be added and three times the amount of the cellulose nanofibers to be added is from 15 to 90.
1. A power transmission belt comprising a rubber composition, wherein
the rubber composition contains a rubber component, cellulose nanofibers, carbon black, and short fibers,
the amount of the cellulose nanofibers to be added is from 0.1 parts by mass to 20 parts by mass, relative to 100 parts by mass of the rubber component,
the amount of the carbon black to be added is 5 parts by mass or more, relative to 100 parts by mass of the rubber component, and
the sum of the amount of the carbon black to be added and three times the amount of the cellulose nanofibers to be added is from 25 to 43.
2. The power transmission belt of claim 1 , wherein the cellulose nanofibers have an average fiber diameter from 1 nm to 200 nm.
3. The power transmission belt of claim 1 , wherein the carbon black has a nitrogen specific surface area of 120 m 2 /g or less.
4. The power transmission belt of claim 1 , wherein
the rubber component comprises at least one material selected from a group of materials consisting of: an ethylene propylene copolymer, an ethylene-propylene-diene terpolymer, an ethylene-octene copolymer, and ethylene-butene copolymer, a chloroprene rubber, a chlorosulfonated polyethylene rubber, and a hydrogenated acrylonitrile rubber.
5. The power transmission belt of claim 1 , wherein
the cellulose nanofibers comprises TEMPO-oxidized cellulose nanofibers.
6. The power transmission belt of claim 1 , wherein
the fiber diameters of the short fibers are from 5.0 μm to 70 μm.