Processing method for biopolymers using solvent combinations
The invention relates primarily to a processing method of biopolymers by means of solvent/solvent mixtures or multiphase solvent systems by means of which said polymers can be changed in their mechanical and qualitative features and processed more easily.
1. A method of processing a biopolymer, comprising:
providing the biopolymer in dry particulate form, wherein the biopolymer is hyaluronic acid or a hyaluronate salt;
optionally providing at least one active pharmaceutical ingredient;
providing a single-phase solvent solution consisting of 30%-40% water and 60%-70% isopropanol or ethanol;
combining the biopolymer in dry particulate form with the single-phase solvent solution, and optionally the at least one active pharmaceutical ingredient; and
mixing the combined mixture by mechanical means to produce a biopolymer matrix having a homogenous swelling.
2. The method of claim 1 , further comprising removing excess isopropanol or ethanol from the produced biopolymer matrix by pressure and/or air circulation.
3. The method of claim 1 , further comprising forming a pressed body from the biopolymer matrix.
4. The method of claim 3 , wherein the pressed body is microneedles or a film.
5. The method of claim 1 , further comprising pressing the biopolymer matrix in a cavity or mold, and drying and/or solidifying before or after removal from the cavity or mold.
6. The method of claim 5 , wherein the cavity or mold is shaped for microneedles.
7. The method of claim 1 , further comprising forming a film from the biopolymer matrix.
8. The method of claim 7 , further comprising applying the film to a bandage or plaster base.
9. The method of claim 1 , wherein the biopolymer in dry particulate form and the single-phase solvent solution are combined in an amount of about 0.60-0.61 g biopolymer to about 1 ml solvent solution.
10. The method of claim 1 , wherein the at least one active pharmaceutical ingredient is provided.
11. The method of claim 1 , wherein the method is carried out under sterile conditions to produce a sterile biopolymer matrix.