Method for preparing fine bamboo powder
A MATZHU is prepared by using leaves of Gramineae (Graminae) and Bambusoideae plant as raw materials. The MATZHU has a stable emerald color and an average powder particle size of 800 to 10,000 meshes. The MATZHU also has a total amount of dietary fiber of ≥60%, a content of lignin of ≥20% and a content of minerals of ≥7%. The MATZHU includes at least three or more bamboo leaf characteristic components, such as orientin, isoorientin, vitexin, isovitexin, adenosine, δ-hydroxylysine and p-coumaric acid. The method for the MATZHU preparation includes, in turn, performing blanching and color protection, drying and superfine grinding the raw materials. By utilizing the thermal stability and the light stability of the MATZHU, the MATZHU may be used as a raw food material, a functional ingredient, or a dietary supplement.
1. A method for preparing MATZHU, comprising the following steps:
(1) blanching and color protecting raw materials;
(2) drying the raw materials resulting from step (1) to obtain dried raw materials; and
(3) superfine grinding the dried raw materials, to obtain the MATZHU having an average particle size of 1000-10,000 mesh;
wherein the raw materials are leaves of Gramineae (Graminae) and Bambusoideae plant;
wherein the blanching and color protecting step comprises: putting bamboo leaves as raw materials into a color-protecting solution with a temperature of 85 to 95° C., taking out after soaking for 30 to 90 seconds, and draining; and
wherein the color-protecting solution used in the blanching and color protecting step is a zinc sulfate aqueous solution or a zinc gluconate aqueous solution or a combination thereof with a concentration of 0.5 to 2.0 g/100 mL.
2. The method of claim 1 , wherein a material-to-liquid ratio of the bamboo leaf and the color protection liquid is 1 g: 50-100 mL.
3. The method of claim 1 , wherein the drying of step (2) is drying the leaves after the blanching and color protecting step to a moisture content of ≤11%; and
wherein the drying of step (2) uses at least one of hot air drying, microwave drying, vacuum drying and freeze drying.
4. The method of claim 1 , wherein the source of the raw materials is fresh leaves of Zhejiang henon bamboo ( Phyllostachys meyeri McClure), moso bamboo ( Phyllostachys heterocycla var. puhescens (Mazel) Ohwi), Neosinocalamus affinis ( N.affinis (Rendle) Keng f.) Mian bamboo ( B. intermedia Hsueh et Yi), Sulfur Yu bamboo ( Yushania Keng f.), bitter bamboo ( P. amarus (keng) Keng f.), Bashania fangiana ( B.fangiana Keng f. et Wen) and sasa argenteastriatus ( Pleiohlastus kongosanensis f.aureostriaus ).
5. The method of claim 1 , wherein
wherein the superfine grinding of step (3) comprises one of the following: high-energy nano-impact ball grinding, wherein the grinding ball is a zirconium ball, and ball-to-material ratio is 10:1; fluid energy grinding; or fluid energy grinding+high-energy nano-impact ball grinding.