Method for impregnation a polymeric granulate with a physical blowing agent
A method for impregnating a polymeric granulate with a physical blowing agent is disclosed. The polymeric granulate can be a typical material such as a polycarbonate that is used in foam injection moulding processes. The physical blowing agent can be carbon dioxide which impregnates that polymeric granulate at a temperature range of 40° to 120° C. and a pressure range of 15 to 55 bar. Preferably, the polymeric granulate is heated in a range of 50° to 90° with a range of 60° to 80° preferred. A pressure range of 25 to 45 bar is preferred with a range of 30 to 40 bar more preferred.
1. A method for impregnating a polymeric granulate with a physical blowing agent for an injection moulding process, comprising:
drying the polymeric granulate at a temperature of from between 40° C. and 130° C., optionally of from between 50° C. and 90° C.,
impregnating the polymeric granulate with the physical blowing agent at a temperature of from 40° C. to 120° C. and at a pressure of from 15 to 55 bar before the injection moulding process in an injection moulding machine, and
processing the polymeric granulate in the injection moulding machine with the physical blowing agent from the impregnating remaining in the polymeric granulate during the processing.
2. The method of claim 1 wherein the physical blowing agent comprises carbon dioxide.
3. The method of claim 1 wherein the polymeric granulate is selected from the group consisting of thermoplastic resins, thermoset resins, thermoplastic particle foams, granulate for production of thermoplastic particle foams, polypropylene, expanded polypropylene (EPP), polystyrene, expanded polystyrene, and polycarbonate.
4. The method of claim 1 wherein the temperature of at least one of the drying the polymeric granulate and the impregnating the polymeric granulate with the physical blowing agent is selected from the group consisting of 50° C. to 90° C. and 60° C. to 80° C.
5. The method of claim 1 wherein the pressure is selected from the group consisting of 25 bar to 45 bar and 30 bar to 40 bar.
6. The method of claim 1 further comprising cooling the polymeric granulate after the impregnating.
7. The method of claim 1 further comprising storing the polymeric granulate in a carbon dioxide atmosphere.
8. The method of claim 7 wherein the storing the polymeric granulate is at ambient pressure of from 1 bar to 10 bar, optionally from 2 bar to 5 bar.
9. The method of claim 7 further comprising locating the carbon dioxide atmosphere in a hopper of an injection moulding machine for the injection moulding process.