A composition for exhaust gas purification containing Y—Mn—O and Al 2 O 3 and having a specific surface area (SSA) retention satisfying inequality (1) SSA retention (%) >−61.54×(Y—Mn—O ratio)+75.55 and inequality (2) SSA retention (%) >45 (2), where SSA retention is represented by (SSA after aging)/(initial SSA)×100 (%). The SSA after aging and the initial SSA are as defined in the description. The Y—Mn—O ratio is a mass ratio of Y—Mn—O to the sum of Y—Mn—O and Al 2 O 3 in the composition for exhaust gas purification, being represented by Y—Mn—O/(Y—Mn—O+Al 2 O 3 ).
1. A composition for exhaust gas purification comprising an yttrium-manganese composite oxide and Al 2 O 3 and having a specific surface area (SSA) retention satisfying inequalities (1) and (2):
SSA retention (%)>−61.54×(Y—Mn—O ratio)+75.55 (1)
SSA retention (%)>45 (2)
wherein SSA retention is represented by (SSA after aging)/(initial SSA)×100 (%); initial SSA is the SSA (m 2 /g) of a composition for exhaust gas purification having been subjected to a heat treatment at 500° C. for 1 hour followed by no further heat treatment; SSA after aging is the SSA (m 2 /g) of the composition for exhaust gas purification having been subjected to a heat treatment at 500° C. for 1 hour followed by another heat treatment at 980° C. for 25 hours; Y—Mn—O represents the yttrium-manganese composite oxide; and Y—Mn—O ratio is a mass ratio of the Y—Mn—O to the sum of the Y—Mn—O and Al 2 O 3 in the composition for exhaust gas purification, being represented by Y—Mn—O/(Y—Mn—O+Al 2 O 3 ).
2. The composition according to claim 1 , wherein the Y—Mn—O ratio is in the range of from 0.1 to 0.9.
3. The composition according to claim 1 , wherein the Y—Mn—O has a particle diameter D50 of 6 μm or smaller, the D50 being a particle diameter at 50% of a cumulative particle size distribution on a volume basis as measured by laser diffraction particle size analysis.
4. The composition according to claim 1 , wherein the Al 2 O 3 is θ-alumina.
5. A catalyst for exhaust gas purification comprising the composition according to claim 1 and a catalyst active component, the catalyst active component comprising at least one element selected from Ag, Mn, Ni, Pt, Pd, Rh, Au, Cu, Fe, and Co.