Resorbable implantable device based on crosslinked glycosaminoglycans, and process for the preparation thereof
Disclosed is a process for the preparation of hydrogels consisting of crosslinked glycosaminoglycans, which comprises: a) reacting at least one hybrid cooperative complex obtained by heating aqueous solutions of low- and high-molecular-weight glycosaminoglycans at 80-160° C. with a diepoxide as crosslinker in a ratio with the complex ranging between 0.1 and 1 equivalents, preferably between 0.2 and 0.4 equivalents, the concentration by weight of the complex in the solution ranging between 1% and 15%, preferably between 2% and 10%; b) purifying by dialysis, ultrafiltration and diafiltration.
1. A process for the preparation of hydrogels consisting of crosslinked glycosaminoglycans which comprises:
a) reacting an aqueous solution of at least one hybrid cooperative complex between a first component selected from low-molecular-weight hyaluronic acid, chondroitin and chondroitin sulphate and a second component consisting of high-molecular-weight hyaluronic acid with a diepoxide as crosslinker in an 0.1 to 1 equivalent ratio to the complex, the weight concentration of the complex in the solution ranging from 1% to 15%;
b) purifying by dialysis, ultrafiltration and diafiltration,
wherein:
the hybrid cooperative complex is prepared by subjecting the aqueous solution of a mixture of said first and second components to heat treatment at 80-160° C. for a time ranging between 10 and 30 minutes, followed by cooling to 20-25° C. in a time ranging between 5 and 15 minutes;
the concentration by weight of the first component with low molecular weight ranges between 0.1 and 50%, and the concentration by weight of the second component with high molecular weight ranges between 0.01 and 10%;
wherein the molecular weight of the low-molecular-weight hyaluronic acid ranges from 50·103 Da to 900·103 Da, the molecular weight of the chondroitin or chondroitin sulphate ranges from 5000 to 150,000 Da, and the molecular weight of the high-molecular-weight hyaluronic acid ranges from 1·106 Da to 3·106 Da (MW obtained by SEC and/or SEC-TDA),
wherein the ultrafiltration is carried out with 1 to 10 diafiltration volumes at a permeation rate ranging from 0.1 L/h to 10 L/h, with ΔP from 1 to 2 bars, using a hollow fibre membrane with cut-off from 250 to 750 KDa.
2. The process according to claim 1 wherein the reaction is carried out at a temperature ranging from 10° C. to 50° C., for reaction times ranging from 2 h to 48 h.
3. The process according to claim 1 wherein the number of hybrid complexes is 1 to 4.
4. The process according to claim 1 wherein both the glycosaminoglycans are high- and low-molecular weight hyaluronic acid.
5. The process according to claim 1 wherein the low-molecular-weight glycosaminoglycan is chondroitin or chondroitin sulphate.
6. The process according to claim 1 wherein the diepoxide is 1,4-butanediol-diglycidyl-ether.
7. The process according to claim 1 wherein the purification steps are carried out at temperature gradients ranging from 10° C. to 58° C.
8. The process according to claim 1 wherein dialysis is carried out with cellulose membranes with cut-off ranging from 10 KDa to 50 KDa and using purified water or phosphate buffer with osmolarity ranging from 200 mOsm/L to 400 mOsm/L as dialysis medium.
9. The process according to claim 7 , wherein the purification steps are carried out at temperature gradients ranging from 20° C. to 50° C.