Provided is a method for separating copper from nickel and cobalt, which can efficiently and selectively separate copper from nickel and cobalt in a substance containing copper, nickel, and cobalt in a waste lithium ion battery, etc. In this method, a substance containing copper, nickel, and cobalt is sulfurated to obtain a sulfide, the obtained sulfide that contains copper, nickel, and cobalt is brought into contact with an acid solution to obtain a solid containing copper and a leachate containing nickel and cobalt. The sulfide preferably contains copper sulfide as a main component, and contains nickel metal and cobalt metal. In-addition, when bringing the sulfide into contact with the acid solution, the added amounts of the sulfide and the acid solution are preferably adjusted such that the oxidation-reduction potential of the obtained leachate is maintained at 150 mV or less where a silver/silver chloride electrode is a reference electrode.
1. A method for separating copper from nickel and cobalt, the method comprising:
sulfurizing a material containing copper, nickel, and cobalt to obtain a sulfide-containing copper sulfide as a main component and also containing nickel metal and cobalt metal;
bringing the obtained sulfide into contact with an acid solution, which is a solution containing at least one selected from the group consisting of sulfuric acid, hydrochloric acid and nitric acid, to obtain a solid containing copper sulfide and a leachate containing nickel and cobalt; and
wherein when the sulfide is brought into contact with the acid solution, adjusting addition amounts of the sulfide and the acid solution, such that an oxidation-reduction potential of the obtained leachate is maintained at a value of 150 mV or less where a silver/silver chloride electrode is a reference electrode.
2. The method for separating copper from nickel and cobalt according to claim 1 , wherein the material containing copper, nickel, and cobalt is obtained by heating, melting, and reducing a waste lithium ion battery.
3. The method for separating copper from nickel and cobalt according to claim 1 , wherein the sulfide has a powder form having a particle diameter of 300 μm or less.
4. The method for separating copper from nickel and cobalt according to claim 1 , wherein after the solid containing copper sulfide and the leachate containing nickel and cobalt are separated, a treatment of removing copper remaining in the leachate is performed.
5. The method for separating copper from nickel and cobalt according to claim 4 , wherein copper remaining in the leachate is removed by one or more types of methods selected from a sulfurizing treatment, an electrowinning treatment, and a neutralizing and precipitating treatment.