Metallic components with enhanced mechanical strength through surface mechanical grinding
A method of strengthening a component made of a metallic material. The method includes subjecting the component to a mechanical grinding process incorporating a relative motion between a tool and the component forming a gradient structure on the surface of the component, resulting in increased tensile strength of the component. A method of strengthening a component made of a TWIP steel. The method includes subjecting the component made of TWIP steel to a mechanical grinding process incorporating a relative motion between a tool and the component forming a gradient structure containing a surface nanolaminate layer, a shear band layer, and an inner deformation twinned layer, resulting in increased tensile strength of the component. A component made of a TWIP steel containing a gradient structure with a surface nanolaminate layer, a shear band layer, and a deformation twinned layer.
1. A component made of a TWIP steel comprising gradient structure containing a surface nanolaminate layer, a shear band layer, and a deformation twinned layer.
2. The component of claim 1 , wherein the shear band layer has a twin spacing in the range of 10 nm to 80 nm.
3. The component of claim 2 , wherein the shear band layer contains deformation twins.
4. The component of claim 3 , wherein the deformation twins have a twin spacing in the range of 10 nm to 80 nm.
5. The component of claim 1 , wherein the surface nanolaminate layer has gradient structure wherein the grain size varies from 10 nm to 100 nm.
6. The component of claim 5 , wherein the surface nanolaminate layer has gradient structure wherein the grain size varies from 15 nm to 60 nm.
7. The component of claim 1 , wherein the deformation twinned layer has a twin spacing in the range of 10 nm to 100 micrometers.
8. The component of claim 7 , wherein the deformation twinned layer has a twin spacing in the range of 10 nm to 10 micrometers.
9. The component of claim 1 , wherein the component made of TWIP steel has tensile strength is in the range of 350 MPa to 600 Mpa.
10. The component of claim 1 , wherein the component is an automotive body component.