Soft magnetic alloy embodiments for additive manufacturing and geometric structures formed therefrom
Disclosed herein are embodiments of soft magnetic alloy embodiments for use in additive manufacturing and structures fabricated from such alloys. In some embodiments, the fabricated structures comprise a continuous thin wall (or plurality thereof) having a geometry that promotes reduced eddy current losses and other performance enhancements. In some embodiments, the fabricated structures are used to make components, such as transformer cores and/or electric motors.
1. An additively manufactured object having a shape, comprising:
a continuous thin wall having a thickness ranging from greater than 0 mm to 1.5 mm and that occupies a fixed region of the object defined by the shape of the object, wherein the continuous thin wall is made of an iron-silicon alloy and comprises at least two termini that do not physically touch, and wherein external boundaries of the continuous thin wall do not touch along a path length of the continuous thin wall; and
an internal void region defined by the external boundaries of the continuous thin wall.
2. The additively manufactured object of claim 1 , wherein the iron-silicon alloy comprises silicon in an amount ranging from 3 wt % to 6 wt %.
3. The additively manufactured object of claim 1 , wherein the iron-silicon alloy is not Fe-6.9Si.
4. The additively manufactured object of claim 1 , wherein the continuous thin wall has a path length that reduces eddy current loop formation.
5. The additively manufactured object of claim 1 , wherein the continuous thin wall is configured in a pattern that comprises at least one angled curve.
6. The additively manufactured object of claim 5 , wherein the angled curve ranges from greater than 0° to less than 180°.
7. The additively manufactured object of claim 1 , wherein the continuous thin wall is fabricated to have a geometry that adopts a Hilbert curve pattern.
8. The additively manufactured object of claim 1 , wherein the continuous thin wall is fabricated to have a shape matching a square spiral pattern.
9. The additively manufactured object of claim 1 , wherein the iron-silicon alloy is substantially free of carbon or oxygen interstitial elements.
10. The additively manufactured object of claim 1 , wherein the additively manufactured object is a structural component of a transformer core or an electric motor.
11. The additively manufactured object of claim 1 , wherein the continuous thin wall does not comprise a single planar sheet of the iron-silicon alloy or a plurality of laminated planar sheets of the iron-silicon alloy.
12. A method for manufacturing the additively manufactured object of claim 1 , the method comprising:
(a) adding a first amount of an iron-silicon alloy feedstock to a build platform;
(b) exposing the first amount, or a portion thereof, of the iron-silicon alloy feedstock to an energy source to provide a first energy-treated region on the build platform, wherein the first energy-treated region comprises an iron-silicon alloy material;
(c) adding a second amount of the iron-silicon alloy feedstock to the build platform, wherein the second amount of the iron-silicon alloy feedstock is positioned immediately adjacent to the first energy-treated region on the build platform;
(d) exposing the second amount, or a portion thereof, of the iron-silicon alloy feedstock to the energy source to provide a second energy-treated region on the build platform, wherein the second energy-treated region comprises the iron-silicon alloy material; and repeating steps (a), (b), (c), and/or (d) to fabricate the continuous thin wall made up of the iron-silicon alloy material.
13. The method of claim 12 , further comprising pre-heating a build plate upon which the iron-silicon alloy feedstock is added during fabrication.
14. The method of claim 12 , further comprising increasing or decreasing cooling rate to change a thickness of the continuous thin wall.
15. The method of claim 12 , wherein a scan pattern is used to modify a grain structure of the iron-silicon alloy material during fabrication.
16. The method of claim 12 , wherein the iron-silicon alloy is Fe-3Si or Fe-6Si.
17. The method of claim 12 , wherein the iron-silicon alloy feedstock is in the form of a powder.
18. An additively manufactured transformer core, or part thereof, comprising:
a continuous thin wall made of an Fe-3Si or an Fe-6Si alloy and having a thickness ranging from 0.1 mm to 1.5 mm and that comprises (i) a first terminus and a second terminus, wherein the first terminus and the second terminus do not physically touch and (ii) an external boundary; and
an internal void region defined by the external boundary of the continuous thin wall; wherein the continuous thin wall comprises at least one angled curve ranging from greater than 0° to 90°.