Magnesium oxide-polyamine adsorbent and a method of capturing carbon dioxide
An aminated magnesium oxide adsorbent containing a magnesium oxide matrix having disordered mesopores and a BET surface area of 320 to 380 m 2 /g, and a polyamine selected from the group consisting of an ethyleneamine having a molecular weight of up to 450 g/mol and a polyethylene imine having a number average molecular weight of greater than 500 g/mol and up to 20,000 g/mol, wherein the polyamine is impregnated within the disordered mesopores of the magnesium oxide matrix. A method of making the aminated magnesium oxide adsorbent and a method of capturing CO 2 from a gas mixture with the aminated magnesium oxide adsorbent are also described.
1. An aminated magnesium oxide adsorbent, comprising:
a magnesium oxide matrix having disordered mesopores and a BET surface area of 320 to 380 m 2 /g; and
a polyamine selected from the group consisting of an ethyleneamine having a molecular weight of up to 450 g/mol and a polyethylene imine having a number average molecular weight of greater than 500 g/mol and up to 20,000 g/mol;
wherein the polyamine is impregnated within the disordered mesopores of the magnesium oxide matrix.
2. The aminated magnesium oxide adsorbent of claim 1 , wherein the magnesium oxide matrix is prepared from precipitation of magnesium hydroxide from a solution of a magnesium salt and ammonium hydroxide, followed by calcination of the magnesium hydroxide at 350 to 450° C.
3. The aminated magnesium oxide adsorbent of claim 1 , wherein the magnesium oxide matrix has an average pore volume of 0.3 to 0.5 cm 3 /g and an average pore size of 3 to 6 nm.
4. The aminated magnesium oxide adsorbent of claim 1 , wherein the magnesium oxide matrix consists essentially of magnesium oxide.
5. The aminated magnesium oxide adsorbent of claim 1 , wherein the polyamine is the ethyleneamine.
6. The aminated magnesium oxide adsorbent of claim 5 , wherein the ethyleneamine is at least one selected from the group consisting of diethylenetriatnine, triethylentetramine, tetraethylenepentamine, pentaethylene hexamine, and hexaethylene heptamine.
7. The aminated magnesium oxide adsorbent of claim 5 , wherein the ethyleneamine is diethylenetriamine.
8. The aminated magnesium oxide adsorbent of claim 1 , wherein the polyamine is the polyethylene imine, and the polyethylene imine is a linear polyethylene imine.
9. The aminated magnesium oxide adsorbent of claim 1 , which has a magnesium content of 15 to 31 wt. %, an oxygen content of 40 to 50 wt. %, a carbon content of 17.5 to 30 wt. %, and a nitrogen content of 2 to 16 wt. %, each based on a total weight of the aminated magnesium oxide adsorbent.
10. The aminated magnesium oxide adsorbent of claim 1 , which has a BET surface area of 40 to 98 m 2 /g.
11. The aminated magnesium oxide adsorbent of claim 1 , which has an average pore size of 7 to 11 nm.
12. The aminated magnesium oxide adsorbent of claim 1 , which has an average pore volume of 0.05 to 0.3 cm 3 /g.
13. The aminated magnesium oxide adsorbent of claim 1 , which is crystalline by XRD.
14. The aminated magnesium oxide adsorbent of claim 1 , which has a CO 2 uptake capacity of 24 to 60 mg CO 2 per 1 g of the aminated magnesium oxide adsorbent at 30° C. and 1 atm.
15. A method of making the aminated magnesium oxide adsorbent of claim 1 , the method comprising:
precipitating magnesium hydroxide from a solution of a magnesium salt and ammonium hydroxide;
calcining the magnesium hydroxide at 350 to 450° C. for 6 to 24 hours to form the magnesium oxide matrix having disordered mesopores; and
wet impregnating the magnesium oxide matrix with an alcoholic solution of the polyamine.
16. The method of claim 15 , wherein a molar ratio of the ammonium hydroxide to the magnesium salt in the solution is 2:1 to 9:1, and wherein the precipitating is performed by heating the solution to 50 to 70° C. for 3 to 10 hours, followed by stirring the solution at 20 to 30° C. for 12 to 48 hours.
17. The method of claim 15 , wherein a weight ratio of the polyamine to the magnesium oxide matrix for the wet impregnating is 1:1 to 1:3.
18. A method of capturing CO 2 from a gas mixture comprising CO 2 and at least one other gas selected from the group consisting of hydrogen, oxygen, nitrogen, methane, and carbon monoxide, the method comprising:
contacting the gas mixture with the aminated magnesium oxide adsorbent of claim 1 to adsorb at least a portion of the CO 2 into the aminated magnesium oxide adsorbent, thereby forming a loaded aminated magnesium oxide adsorbent and a gas stream depleted in CO 2 compared to the gas mixture.
19. The method of claim 18 , wherein the gas mixture is a pre-combustion gas mixture comprising 15 to 50 vol. % of CO 2 , based on a total volume of the gas mixture.
20. The method of claim 18 , wherein the gas mixture is a post-combustion gas mixture comprising 5 to 15 vol. % of CO 2 , based on a total volume of the gas mixture.