High pressure decorative laminate having a top layer of energy cured acrylated urethane polymer
A laminate lay-up includes a coated decorative paper layer having a decorative paper layer with a textured coating layer applied thereto. The textured coating layer is comprised of a UV curable coating composition. The laminate lay-up also includes a decorative layer and a core layer.
1. A laminate lay-up, comprising:
a decorative layer comprising a coated decorative paper layer consisting of an untreated decorative paper layer, of alpha cellulose paper having a basis weight of approximately 50 grams per square meter to 200 grams per square meter, and textured coating layer comprised of a UV curable coating composition including an energy cured acrylated urethane polymer applied thereto; and
a core layer.
2. The laminate lay-up according to claim 1 , wherein the energy cured acrylated urethane polymer includes acrylate and acrylated urethane oligomers, before final polymerization.
3. The laminate lay-up according to claim 1 , further including a low basis weight paper that has been impregnated with melamine-formaldehyde resin positioned beneath the coated decorative paper layer.
4. A decorative laminate manufactured by the method consisting essential of:
applying a UV curable coating composition including an energy cured acrylated urethane polymer to an untreated decorative paper layer of alpha cellulose paper having a basis weight of approximately 50 grams per square meter to 200 grams per square meter;
irradiating the UV curable coating composition with LED precure by excimer UV to create a UV-irradiated layer having a surface exhibiting micro-folding;
partially curing the UV-irradiated layer to form a UV cured coating on the decorative paper layer;
forming a laminate lay-up including the decorative paper layer with the UV cured coating; and
applying heat and pressure to consolidate the laminate lay-up and form the decorative laminate.
5. The decorative laminate according to claim 4 , wherein the step of irradiating is includes treating the UV curable coating composition so that the UV curable coating composition is only crosslinked on a surface thereof to produce a supermatting surface through micro-convolution.
6. The decorative laminate according to claim 5 , wherein the step of irradiating is achieved with an excimer emitter based on a Xe-emission spectrum at a wavelength of 172 nm in a presence of nitrogen.
7. The laminate lay-up according to claim 6 , wherein the energy cured acrylated urethane polymer includes acrylate and acrylated urethane oligomers, before final polymerization.
8. The decorative laminate according to claim 7 , wherein the step of partially curing is achieved by E-beam or UV irradiation.
9. The decorative laminate according to claim 4 , wherein the step of irradiating is achieved with an excimer emitter based on a Xe-emission spectrum at a wavelength of 172 nm in a presence of nitrogen.
10. The decorative laminate according to claim 4 , wherein the step of partially curing is achieved by E-beam or UV irradiation.