Method of making an in situ sustained biodegradable drug delivery implant by filling an artificial tissue cavity
This invention discloses methods and composition to form biodegradable polymer implant arrays in the live tissue. Artificial cavities are created in the live tissue by using laser ablation, oscillating needle, microneedle array and other methods. The cavities are then filled with biodegradable polymer solution. The solvent in the polymer solution is dissipated in the tissue to form a biodegradable polymer implant in artificial cavities. The cavities and implants formed are arranged to form of an array of implants. The biodegradable polymer in the cavity can also be loaded with drug to form biodegradable drug delivery array in the live tissue.
1. A method of making a sustained biodegradable drug delivery implant in a live tissue, the method comprising:
creating at least two artificial cavities of predetermined shape and volume in the live tissue;
filling the at least two artificial cavities partially or completely with an injectable biodegradable composition comprising a biodegradable polymer dissolved in a biocompatible, water-soluble organic solvent; and
precipitating the polymer from the injected polymer solution so as to form the sustained biodegradable implant in the artificial cavity.
2. The method of claim 1 , further comprising forming at least 4 artificial cavities per square centimeter in the live tissue.
3. The method of claim 1 , further comprising forming from 4 artificial cavities to 6,000 artificial cavities per square centimeter in the live tissue.
4. The method of claim 1 , wherein a volume of each cavity may range from about 1×10E-12 ml to about 0.05 ml.
5. The method of claim 3 , further comprising forming an array of the artificial cavities in the live tissue.
6. The method of claim 3 , further comprising forming the cavities to have a spacing between adjacent cavities to range from 1 micron to 10 mm.
7. The method of claim 3 , wherein the creating of the artificial cavitites further comprises displacing tissue, destroying tissue, or combination thereof.
8. The method of claim 1 , wherein the creating of the artificial cavitites further comprises laser ablation, microneedle array, oscillating needle, mechanical drilling, ultrasonic drilling, water drilling, or combination thereof.
9. The method of claim 1 , wherein the tissue is skin tissue.
10. The method of claim 1 , wherein the biocompatible, water-soluble organic solvent is selected from a group consisting of tripropionin (triprop), tetraglycol, pyrrolidone-2, ethyl lactate, triacetin, triethylene glycol dimethyl ether (triglyme), glycerol formal, dimethyl sulfoxide, ethylene glycol monoethyl ether acetate, benzyl alcohol, n-methyl pyrrolidone, N-ethyl-2-pyrrolidone, tributyrin, benzyl benzoate, acetone, methyl ethyl ketone, acetic acid, ethanol, isopropanol, diethylene glycol dimethyl ether (Diglyme), ethyl benzoate, dimethyl isosorbide (DMI), polyethylene glycol dimethyl ether, glycofurol, glycerol, ethyl acetate, polyethylene glycol (low molecular weight), 1,3 propane diol, 1,4 butane diol, 1-6-hexane diol, tetrahydrofuran, triethanol amine, water, buffered water solutions with pH ranging from 6 to 8, and combinations thereof.
11. The method of claim 1 , wherein a concentration of the biocompatible polymer in the biocompatible, water-soluble organic solvent ranges from about 0.1% to about 60%.
12. The method of claim 1 , wherein the injectable biodegradable composition and formed implant comprises a visualization agent.
13. The method of claim 12 , wherein the visualization agent is a colored compound, a fluorescent compound, an x-ray imaging agent, radio opaque contrast agent, NMR contrast agent, or a MRI agent.
14. The method of claim 1 , comprising injecting the injectable biodegradable composition into the tissue at a depth of about 10 microns to about 5 mm.
15. The method of claim 1 , wherein the injectable biodegradable composition and formed implant comprises a drug.
16. The method of claim 15 , wherein the drug is dissolved, suspended, or emulsified in the injectable composition before the filing of the at least two cavitites.
17. The method of claim 16 , wherein the drug is present at a drug concentration of about 1% to 40% relative to polymer weight of the biodegradable polymer in polymer solution or formed implant.
18. The method of claim 15 , wherein the drug is selected from the group consisting of: antiinfectives, antibiotics; antiviral agents, antifungal agents, antibacterial agents, antipruritics; anticancer agents, antipsychotics; cholesterol- or lipid-reducing agents; cell cycle inhibitors; anticancer agents; antiparkinsonism drugs; HMG-CoA inhibitors; antirestenosis agents; antiinflammatory agents; antiasthmatic agents; anthelmintic; immunosuppressives; muscle relaxants; antidiuretic agents; vasodilators; nitric oxide; nitric oxide-releasing compounds; beta-blockers; hormones; antidepressants; decongestants; calcium channel blockers; growth factors, bone growth factors or bone morphogenic proteins; wound healing agents; analgesics and analgesic combinations; local anesthetic agents; antihistamines; sedatives; angiogenesis-promoting agents; angiogenesis-inhibiting agents; tranquilizers; and combinations thereof.
19. The method of claim 1 , further comprising forming the at least two cavities to have a depth of about 0.3 microns to about 3.5 mm.
20. The method of claim 1 , further comprising injecting the injectable biodegradable composition into the tissue at an amount of 1.0E-02 ml to 1.0E-16 ml per injection.