Lead wire for narrow space insertion
To provide a lead wire for narrow space insertion that is easily inserted into an elongated small-diameter pipe or small-diameter tube such as an ultrasonic probe or an electrode catheter. The above-described problem is solved by a lead wire for narrow space insertion including a copper alloy wire having a conductor diameter within a range of 0.015 to 0.18 mm, and an insulating layer provided to an outer periphery of the copper alloy wire. A friction coefficient of an outermost surface layer of the insulating layer is within a range of 0.05 to 0.3, a tensile strength of the lead wire is within a range of 700 to 1,500 MPa, and a conductivity of the copper alloy wire is within a range of 60 to 90% IACS.
1. A lead wire for insertion by an operator one by one or collectively into a narrow space, comprising:
a copper alloy wire having a conductor diameter within a range of 0.015 to 0.18 mm; and
an insulating layer provided to an outer periphery of the copper alloy wire by baking, a thickness of the insulating layer is 1.0 to 10 μm,
a friction coefficient of only an outermost surface layer of the insulating layer being within a range of 0.05 to 0.3,
a tensile strength of the lead wire being within a range of 700 to 1,500 MPa,
a conductivity of the copper alloy wire being within a range of 60 to 90% International Annealed Copper Standard (IACS);
the outermost surface layer of the insulating layer being a liquid paraffin layer or a nylon layer;
a radius of curvature of the lead wire for narrow space insertion is at least 300 mm or greater; and
the copper alloy wire contains 0.5 to 15 mass % of Ag, with a remaining portion being Cu and inevitable impurities.
2. A lead wire for insertion by an operator one by one or collectively into a narrow space, comprising:
a copper alloy wire having a conductor diameter within a range of 0.015 to 0.18 mm; and
an insulating layer provided to an outer periphery of the copper alloy wire by baking,
a friction coefficient of only an outermost surface layer of the insulating layer being within a range of 0.05 to 0.3,
a tensile strength of the lead wire being within a range of 700 to 1,500 MPa,
a conductivity of the copper alloy wire being within a range of 60 to 90% International Annealed Copper Standard (IACS);
the outermost surface layer of the insulating layer being a liquid paraffin layer or a nylon layer;
a radius of curvature of the lead wire for narrow space insertion is at least 300 mm or greater; and
the copper alloy wire contains 0.5 to 15 mass % of Ag, with a remaining portion being Cu and inevitable impurities.