Positive electrode active material and method of producing positive electrode active material
A method of producing a positive electrode active material, the method includes: contacting first particles that contain a lithium transition metal composite oxide with a solution containing sodium ions to obtain second particles containing the lithium transition metal composite oxide and sodium element, wherein the lithium transition metal composite oxide has a layered structure and a composition ratio of a number of moles of nickel to a total number of moles of metals other than lithium in a range of from 0.7 to less than 1; mixing the second particles and a boron compound to obtain a mixture; and heat-treating the mixture at a temperature in a range of from 100° C. to 450° C.
1. A method of producing a positive electrode active material, the method comprising:
contacting first particles that contain a lithium transition metal composite oxide with a solution containing sodium ions to obtain second particles containing the lithium transition metal composite oxide and sodium element, wherein the lithium transition metal composite oxide has a layered structure and a composition ratio of a number of moles of nickel to a total number of moles of metals other than lithium in a range of from 0.7 to less than 1;
mixing the second particles and a boron compound to obtain a mixture; and
heat-treating the mixture at a temperature in a range of from 100° C. to 450° C.
2. The method according to claim 1 , wherein the second particles have a sodium element content in a range of from 100 ppm to 1400 ppm.
3. The method according to claim 2 , wherein the mixture contains the boron compound in an amount of from 0.1% by mole to 2% by mole in terms of a ratio of a number of moles of boron element relative to the total number of moles of metals other than lithium in the lithium transition metal composite oxide.
4. The method according to claim 3 , wherein the lithium transition metal composite oxide contains cobalt and has a ratio of a number of moles of cobalt to the total number of moles of metals other than lithium in the lithium transition metal composite oxide of 0.3 or less.
5. The method according to claim 4 , wherein the lithium transition metal composite oxide contains at least one of manganese and aluminium and has a ratio of a number of moles of manganese and aluminium to the total number of moles of metals other than lithium in the lithium transition metal composite oxide of 0.3 or less.
6. The method according to claim 1 , wherein the mixture contains the boron compound in an amount of from 0.1% by mole to 2% by mole in terms of a ratio of a number of moles of boron element relative to the total number of moles of metals other than lithium in the lithium transition metal composite oxide.
7. The method according to claim 1 , wherein the lithium transition metal composite oxide contains cobalt and has a ratio of a number of moles of cobalt to the total number of moles of metals other than lithium in the lithium transition metal composite oxide of 0.3 or less.
8. The method according to claim 1 , wherein the lithium transition metal composite oxide contains at least one of manganese and aluminium and has a ratio of a number of moles of manganese and aluminium to the total number of moles of metals other than lithium in the lithium transition metal composite oxide of 0.3 or less.
9. The method according to claim 1 , wherein the lithium transition metal composite oxide has a composition represented by formula (1):
Li (1+p) Ni (1−x−y−z−w) Co x Mn y Al z M w O 2 (1)
wherein −0.05≤p≤0.2, 0<x+y+z+w≤0.3, 0≤x≤0.3, 0≤y≤0.3, 0≤z≤0.1, and 0≤w≤0.03; and M is at least one selected from the group consisting of Zr, Ti, Mg, Ta, Nb, Mo, and W.