Inorganic fiber toughened inorganic composite artificial stone panel and preparation method thereof
An inorganic fiber toughened inorganic composite artificial stone panel and a preparation method thereof are disclosed. The panel includes a surface layer and a toughened base layer. The surface layer includes the the following components in parts by weight: 40-70 parts of quartz sand, 10-30 parts of quartz powder, 20-45 parts of inorganic active powder, 0.5-4 parts of pigment, 0.3-1 parts of water reducing agent and 3-10 parts of water. The toughened base layer includes the following components in parts by weight: 40-60 parts of inorganic active powder, 45-65 parts of sand, 0.8-1.5 parts of water reducing agent, 6-14 parts of water, 0.4-2 parts of inorganic fiber and 0.8-2.5 parts of toughener.
1. An inorganic fiber toughened inorganic composite artificial stone panel, comprising a surface layer and a toughened base layer,
wherein the surface layer includes materials having the following components in parts by weight: 40-70 parts of quartz sand, 10-30 parts of quartz powder, 20-45 parts of an inorganic active powder, 0.5-4 parts of a pigment, 0.3-1 parts of a water reducing agent and 3-10 parts of water,
wherein the toughened base layer includes materials having the following components in parts by weight: 40-60 parts of the inorganic active powder, 45-65 parts of sand, 0.8-1.5 parts of the water reducing agent, 6-14 parts of water, 0.4-2 parts of an inorganic fiber and 0.8-2.5 parts of a toughener, and
wherein the inorganic active powder is mainly composed of pure white Portland cement doped with an active powder, the pure white Portland cement has a strength grade of more than 42.5, and the active powder is at least one selected from the group consisting of white silicon powder, mineral powder, nano calcium oxide, nano silicon oxide, and sintered high white kaolin powder.
2. The inorganic fiber toughened inorganic composite artificial stone panel according to claim 1 , the quartz sand has a fineness modulus of 2.0-3.0, a content of silicon dioxide above 93%, and a hardness of a raw stone above 7.
3. The inorganic fiber toughened inorganic composite artificial stone panel according to claim 1 , the quartz powder has a fineness of 600 mesh or more, a content of silicon dioxide above 93%, and a hardness of a raw stone above 7.
4. The inorganic fiber toughened inorganic composite artificial stone panel according to claim 1 , wherein the sand is selected from one or more of river sand, manufactured sand and the quartz sand.
5. The inorganic fiber toughened inorganic composite artificial stone panel according to claim 1 , wherein the inorganic fiber is selected from one or more of glass fiber, carbon fiber, basalt fiber, boron fiber, ceramic fiber and alumina fiber which have a diameter of 0.02-0.08 mm, a length of 6-12 mm and a tensile strength of more than 1,000 MPa.
6. The inorganic fiber toughened inorganic composite artificial stone panel according to claim 1 , wherein the toughener is selected from one or more of polyvinyl alcohol glue and acrylamide glue.
7. The inorganic fiber toughened inorganic composite artificial stone panel according to claim 1 , wherein a total thickness of the panel is 15-50 mm, and a thickness of the surface layer is 4-6 mm.
8. A preparation method of the inorganic fiber toughened inorganic composite artificial stone panel according to claim 1 , comprising the steps of:
S 1 ) uniformly stirring and mixing first raw materials and second raw materials, respectively, according to the predetermined ratio to obtain a first mixed material and a second mixed material, wherein the first raw materials are used for the surface layer and second raw materials are used for the toughened base layer;
S 2 ) preparing a panel mold, calculating and weighing the first mixed material prepared in step S 1 according to a thickness of the surface layer and uniformly arranging the first mixed material in the panel mold, then calculating and weighing the second mixed material prepared in step S 1 according to a thickness of the toughened base layer and uniformly arranging the second mixed material on the first mixed material in the panel mold;
S 3 ) covering an isolated moisturizing film on the second mixed material in the panel mold of step S 2 , and then putting the panel mold into a vacuum compressor to concurrently perform a vacuum exhaust and a vibrating compression to obtain a compressed plate;
S 4 ) curing the compressed plate obtained in step S 3 at a temperature of 40° C. for 6 to 8 hours, then heating the compressed plate to 80-90° C. and curing the compressed plate at 80-90° C. for 12-16 hours, and obtaining a rough plate; and
S 5 ) performing a bottom scraping, a thickening and a polishing on the rough plate obtained in step S 4 after removing the isolation moisturizing film to obtain the inorganic fiber toughened inorganic composite artificial stone panel.
9. The preparation method according to claim 8 , wherein in step S 1 , time for stirring and mixing the first raw materials and second raw materials is not less than 10 minutes, respectively; Vebe consistency testing time of the first mixed material and the second mixed material is 5-30 seconds, respectively; and the initial setting time of the first mixed material and the second mixed material after the stirring and mixing is not less than 60 minutes.
10. The preparation method according to claim 8 , wherein in step S 3 , time for the vacuum exhaust is not less than 60 seconds, time for the vibrating compression is not less than 120 seconds; and a vacuum pressure for the vacuum exhaust is −0.07-0.1 MPa, a pressure load of the vacuum compressor is not less than 1 MPa, and a pressure of the vacuum compressor is not less than 5000 kN.
11. The preparation method according to claim 8 , wherein in step S 4 , a humidity is kept above 75% during the curing at 80-90° C.
12. The preparation method according to claim 8 , the quartz sand has a fineness modulus of 2.0-3.0, a content of silicon dioxide above 93%, and a hardness of a raw stone above 7.
13. The preparation method according to claim 8 , the quartz powder has a fineness of 600 mesh or more, a content of silicon dioxide above 93%, and a hardness of a raw stone above 7.
14. The preparation method according to claim 8 , wherein the sand is selected from one or more of river sand, manufactured sand and the quartz sand.
15. The preparation method of the inorganic fiber toughened according to claim 8 , the inorganic fiber is selected from one or more of glass fiber, carbon fiber, basalt fiber, boron fiber, ceramic fiber and alumina fiber which have a diameter of 0.02-0.08 mm, a length of 6-12 mm and a tensile strength of more than 1,000 MPa.
16. The preparation method of the inorganic fiber toughened according to claim 8 , wherein the toughener is selected from one or more of polyvinyl alcohol glue and acrylamide glue.
17. The preparation method of the inorganic fiber toughened according to claim 8 , wherein a total thickness of the panel is 15-50 mm, and a thickness of the surface layer is 4-6 mm.
18. An inorganic fiber toughened inorganic composite artificial stone panel, comprising a surface layer and a toughened base layer,
wherein the surface layer includes materials having the following components in parts by weight: 40-70 parts of quartz sand, 10-30 parts of quartz powder, 20-45 parts of an inorganic active powder, 0.5-4 parts of a pigment, 0.3-1 parts of water reducing agent and 3-10 parts of water,
wherein the toughened base layer includes materials having the following components in parts by weight: 40-60 parts of the inorganic active powder, 45-65 parts of sand, 0.8-1.5 parts of the water reducing agent, 6-14 parts of water, 0.4-2 parts of an inorganic fiber and 0.8-2.5 parts of a toughener, and
wherein the quartz powder has a fineness of 600 mesh or more, a content of silicon dioxide above 93%, and a hardness of a raw stone above 7.
19. The inorganic fiber toughened according to claim 18 , the quartz sand has a fineness modulus of 2.0-3.0, a content of silicon dioxide above 93%, and a hardness of a raw stone above 7.
20. The inorganic fiber toughened according to claim 18 , wherein a total thickness of the panel is 15-50 mm, and a thickness of the surface layer is 4-6 mm.