3-dimensional printing
The present disclosure is drawn to material sets for 3D printing and methods of 3D printing. The material set can include a coalescent an organic-soluble near-infrared dye having a peak absorption wavelength from 800 nm to 1400 nm. The coalescent ink can also include water and an organic co-solvent. The material set can also include a particulate polymer formulated to coalesce when contacted by the coalescent ink and irradiated by a near-infrared energy having the peak absorption wavelength.
1. A material set for 3-dimensional powder bed printing, comprising:
a coalescent ink comprising an organic-soluble near-infrared dye having a peak absorption wavelength from 800 nm to 1400 nm, water, and an organic co-solvent; and
a particulate polymer formulated to coalesce when a layer of powder bed of the particulate polymer is:
preheated to about 10° C. to about 30° C. below a melting point or softening point of the particulate polymer,
contacted by the coalescent ink, and
irradiated by a near-infrared energy having the peak absorption wavelength, wherein the particulate polymer is selected from the group consisting of nylon 6 powder, nylon 9 powder, nylon 11 powder, nylon 12 powder, nylon 66 powder, nylon 612 powder, polyethylene powder, thermoplastic polyurethane powder, polypropylene powder, polyester powder, polycarbonate powder, polyether ketone powder, polyacrylate powder, polystyrene powder, and mixtures thereof, and wherein upon adding a layer of the particulate polymer to the powder bed, and then repeating the jetting, the irradiating, and the adding of the layer, a 3-dimensional printed part is formable.
2. The material set of claim 1 , wherein the near-infrared dye is selected from the group consisting of aminium dyes, tetraaryldiamine dyes, cyanine dyes, dithiolene dyes, and combinations thereof.
3. The material set of claim 1 , wherein the near-infrared dye is an aminium dye.
4. The material set of claim 1 , wherein the near-infrared dye does not alter the visible color of the coalescent ink.
5. The material set of claim 1 , wherein the near-infrared dye has a temperature boosting capacity from about 10° C. to about 30° C. for a polymer with a melting point from about 100° C. to about 350° C.
6. The material set of claim 1 , wherein the near-infrared dye has a solubility of about 0.5 wt % to about 5 wt % in water.
7. The material set of claim 1 , wherein the near-infrared dye has a concentration of 0.1 wt % to 25 wt % in the coalescent ink.
8. The material set of claim 1 , wherein the coalescent ink further comprises a pigment in addition to the organic-soluble near-infrared dye, the pigment imparting a visible color to the coalescent ink.
9. The material set of claim 8 , wherein the pigment has a concentration of 1 wt % to 10 wt % in the coalescent ink.
10. The material set of claim 1 , wherein the coalescent ink imparts a visible color when jetted onto polymer particles and provides a concentration of near-infrared dye of 0.1 wt % to 1.5 wt % with respect to the polymer particles.
11. The material set of claim 1 , wherein the particulate polymer has a melting or softening point from about 100° C. to about 350° C.
12. The material set of claim 1 , wherein the near-infrared dye, when printed on a portion of the particulate polymer, has a sufficient temperature boosting capacity so that the printed portion of the particulate polymer increases in temperature by at least 10° C. more than a non-printed portion of particulate polymer when both the printed portion and the non-printed portion are irradiated with a wavelength of about 800 nm to about 1400 nm.
13. A method for forming a 3-dimensional printed part using a material set, comprising a coalescent ink comprising an organic-soluble near-infrared dye having a peak absorption wavelength from 800 nm to 1400 nm, water, and an organic co-solvent; and a particulate polymer formulated to coalesce when contacted by the coalescent ink and irradiated by a near-infrared energy having the peak absorption wavelength; wherein the method further comprises:
preheating a powder bed of the particulate polymer to about 10° C. to about 30° C. below a melting point or softening point of the particulate polymer;
jetting the coalescent ink onto a portion of the powder bed;
irradiating the powder bed with a fusing lamp to emit a wavelength of energy from 800 nm to 1400 nm to cause the portion of the particulate polymer of the powder bed to fuse;
adding a layer of the particulate polymer to the powder bed; and
repeating the jetting, the irradiating, and the adding of the layer to form the 3-dimensional printed part.
14. The method of claim 13 , wherein the near-infrared dye is selected from the group consisting of aminium dyes, tetraaryldiamine dyes, cyanine dyes, dithiolene dyes, and combinations thereof.
15. A material set for 3-dimensional powder bed printing, comprising:
a coalescent ink comprising an organic-soluble near-infrared dye having a peak absorption wavelength from 800 nm to 1400 nm, water, and an organic co-solvent; and
a particulate polymer formulated to coalesce when a layer of powder bed of the particulate polymer is:
preheated to about 10° C. to about 30° C. below a melting point or softening point of the particulate polymer,
contacted by the coalescent ink, and
irradiated by a near-infrared energy having the peak absorption wavelength,
wherein the particulate polymer has a melting or softening point from about 100° C. to about 350° C., and wherein upon adding a layer of the particulate polymer to the powder bed, and then repeating the jetting, the irradiating, and the adding of the layer, a 3-dimensional printed part is formable.
16. The material set of claim 15 , wherein the near-infrared dye is selected from the group consisting of aminium dyes, tetraaryldiamine dyes, cyanine dyes, dithiolene dyes, and combinations thereof.
17. The material set of claim 15 , wherein the near-infrared dye does not alter the visible color of the coalescent ink.
18. The material set of claim 15 , wherein the near-infrared dye has a solubility of about 0.5 wt % to about 5 wt % in water.
19. The material set of claim 15 , wherein the coalescent ink further comprises a, pigment in addition to the organic-soluble near-infrared dye, the pigment imparting a visible color to the coalescent ink.
20. The material set of claim 15 , wherein the coalescent ink imparts a visible color when jetted onto polymer particles and provides a concentration of near-infrared dye of 0.1 wt % to 1.5 wt % with respect to the polymer particles.