Graphite sheet having excellent thermal conductivity and method for preparing the same
The present invention provides a method for preparing a high-performance graphite sheet by imidizing a polyamic acid resulting from a reaction of dianhydride monomer(s) and diamine monomer(s) to obtain a polyimide film; and carbonizing and/or graphitizing the polyimide film to obtain a high-performance graphite sheet, where the polyimide film contains 2 or more fillers having different average particle diameters, and the thermal conductivity of the graphite sheet is at least 1,400 W/m·K. Further, the present invention provides a graphite sheet obtained by the above method.
1. A polyimide film for preparing a graphite sheet, the polyimide film comprising:
a first filler having an average particle diameter of 2.0 μm to 2.5 μm, and
a second filler having an average particle diameter of 1.0 μm to 1.6 μm,
wherein the first filler or the second filler is at least one selected from the group consisting of calcium carbonate, calcium phosphate dibasic, and barium sulphate,
wherein the polyimide film is formed by imidizing a polyamic acid; and wherein the first and second fillers have a total content of 2000 ppm to 4000 ppm based on the weight of the polyamic acid, and
wherein the thermal conductivity of the graphite sheet is at least 1,400 W/m·K.
2. The polyimide film for preparing a graphite sheet according to claim 1 , wherein the first and second fillers are sublimated during carbonizing and/or graphitizing step, forming voids in the graphite sheet.
3. The polyimide film for preparing a graphite sheet according to claim 2 , wherein at least parts of the voids form protrusions of extruded shape on the surface of the graphite sheet.
4. The polyimide film for preparing a graphite sheet according to claim 3 , wherein the protrusions have an average particle diameter of less than 0.5 mm.
5. The polyimide film for preparing a graphite sheet according to claim 2 , wherein the graphitizing step is carried out at a temperature of at least 2700° C.
6. The polyimide film for preparing a graphite sheet according to claim 1 , wherein the first or the second fillers are calcium phosphate dibasic and/or barium sulphate.
7. The polyimide film for preparing a graphite sheet according to claim 1 , wherein the polyimide film has an average roughness (Ra) of 8 nm to 30 nm.
8. The polyimide film for preparing a graphite sheet according to claim 1 , wherein the polyimide film contains more than 0% to not more than 40% of the first filler, and at least 60% to less than 100% of the second filler, based on the total of the first and second fillers.
9. The polyimide film for preparing a graphite sheet according to claim 1 , wherein the graphite sheet has a thickness of 15 μm to 40 μm.