Antiglare transparent substrate and display device provided with same
An antiglare transparent substrate includes a transparent substrate which includes a chemically strengthened glass and has a first main surface and a second main surface. The first main surface includes: a first smooth region having an arithmetic average roughness Ra of 0.05 nm or more and 2 nm or less; and a first rough region having an arithmetic average roughness Ra larger than the arithmetic average roughness Ra of the first smooth region. The second main surface includes, in at least a part of a region facing the first smooth region, a second smooth region having an arithmetic average roughness Ra of 0.05 nm or more and 2 nm or less.
1. An antiglare transparent substrate comprising a transparent substrate which comprises a chemically strengthened glass and has a first main surface and a second main surface,
wherein the first main surface comprises:
a first smooth region having an arithmetic average roughness Ra of 0.05 nm or more and 2 nm or less; and
a first rough region having an arithmetic average roughness Ra larger than the arithmetic average roughness Ra of the first smooth region, and
wherein the second main surface comprises, in at least a part of a region facing the first smooth region, a second smooth region having an arithmetic average roughness Ra of 0.05 nm or more and 2 nm or less, and
wherein a surface compressive stress CS of the first smooth region is larger than a surface compressive stress CS of the first rough region.
2. The antiglare transparent substrate according to claim 1 , wherein the arithmetic average roughness Ra of the first rough region is more than 2 nm and 1,000 nm or less.
3. The antiglare transparent substrate according to claim 1 , wherein the second main surface further comprises a second rough region having an arithmetic average roughness Ra larger than the arithmetic average roughness Ra of the second smooth region.
4. The antiglare transparent substrate according to claim 3 , wherein the arithmetic average roughness Ra of the second rough region is more than 2 nm and 1,000 nm or less.
5. The antiglare transparent substrate according to claim 1 , wherein, denoting Z as an atomic composition ratio X/Si of an element X selected from the group consisting of Al, B, Zr, and Ti to Si, Z 1 as the atomic composition ratio Z in the first rough region, and Z 0 as the atomic composition ratio Z in the first smooth region, a ratio Z 1 /Z 0 of Z 1 to Z 0 is from 0 to 1.1.
6. The antiglare transparent substrate according to claim 1 , wherein a skewness (Ssk) of a surface of the first rough region is 0 or more.
7. The antiglare transparent substrate according to claim 6 , wherein the skewness (Ssk) of the surface of the first rough region is 0.2 or more.
8. The antiglare transparent substrate according to claim 1 , wherein a skewness (Ssk) of a surface of the first rough region is less than 0.
9. The antiglare transparent substrate according to claim 8 , wherein the skewness (Ssk) of the surface of the first rough region is less than −0.2.
10. The antiglare transparent substrate according to claim 1 , wherein, assuming a tensile stress to be a positive value and a compressive stress to be a negative value, a plate-thickness-direction stress integrated value S of the first smooth region is less than 0 MPa.
11. The antiglare transparent substrate according to claim 10 , wherein the plate-thickness-direction stress integrated value S of the first smooth region is less than −3 MPa.
12. The antiglare transparent substrate according to claim 1 , wherein the surface compressive stress CS of the first rough region is 500 MPa or more.
13. The antiglare transparent substrate according to claim 1 , wherein the transparent substrate has a thickness of 2 mm or less.
14. The antiglare transparent substrate according to claim 1 , wherein at least a part of the first rough region has a bent portion.
15. A display device comprising the antiglare transparent substrate according to claim 1 .