Multi-layer three-way catalytic converter
The invention relates to a three-way catalytic converter, which is suitable, in particular, for the removal of carbon monoxide, hydrocarbons and nitrogen oxides out of the exhaust gas of combustion engines operated with stoichiometric air-fuel mixture. The three-way catalytic converter is characterized in that it has a high oxygen storage capacity after aging and consists of at least two catalytically active layers.
1. Catalytic converter for removing carbon monoxide, hydrocarbons and nitrogen oxides out of the exhaust gas of combustion engines operated with stoichiometric air-fuel mixture, comprising a ceramic flow substrate of length L and at least two catalytic coatings A and B, wherein
a layer A contains at least one active aluminum oxide, one platinum group metal, and at least two different cerium/zirconium/rare earth metal mixed oxides, and
a layer B applied to layer A contains at least one active aluminum oxide, a platinum group metal, and at least one cerium/zirconium/rare earth metal mixed oxide, and the first cerium/zirconium/rare earth metal mixed oxide in coating A has a weight ratio of cerium oxide to zirconium oxide of 0.7 to 0.1, which is smaller than in the second cerium/zirconium/rare earth metal mixed oxide in coating A, which has a weight ratio of cerium oxide to zirconium oxide of 0.5 to 1.5 and the first cerium/zirconium/rare earth metal mixed oxide in coating A is doped with yttrium oxide in addition to lanthanum oxide.
2. Catalytic converter according to claim 1 , characterized in that
coating A is located on the walls of the substrate and extends from one end of the substrate over at least 50% of the length L.
3. Catalytic converter according to claim 1 , characterized in that
the weight ratio of aluminum oxide to the sum of the two cerium/zirconium/rare earth metal mixed oxides in coating A is in the range from 10:90 to 60:40.
4. Catalytic converter according to claim 1 , characterized in that
the weight ratio of the first cerium/zirconium/rare earth metal mixed oxide to the second cerium/zirconium/rare earth metal mixed oxide in coating A is in the range from 4:1 to 1:4.
5. Catalytic converter according to claim 1 , characterized in that
the first cerium/zirconium/rare earth metal mixed oxide in coating A has a higher zirconium oxide content than the second cerium/zirconium/rare earth metal mixed oxide.
6. Catalytic converter according to claim 1 , characterized in that
the first cerium/zirconium/rare earth metal mixed oxide in coating A has a cerium oxide content of 10% to 40% based on the weight of the first cerium/zirconium/rare earth metal mixed oxide.
7. Catalytic converter according to claim 1 , characterized in that
the first cerium/zirconium/rare earth metal mixed oxide in coating A has a zirconium oxide content of 40% to 90% based on the weight of the first cerium/zirconium/rare earth metal mixed oxide.
8. Catalytic converter according to claim 1 , characterized in that
the second cerium/zirconium/rare earth metal mixed oxide in coating A has a cerium oxide content of 25% to 60% based on the weight of the second cerium/zirconium/rare earth metal mixed oxide.
9. Catalytic converter according to claim 1 , characterized in that
the second cerium/zirconium/rare earth metal mixed oxide in coating A has a zirconium oxide content of 20% to 70% based on the weight of the second cerium/zirconium/rare earth metal mixed oxide.
10. Catalytic converter according to claim 1 , characterized in that
both cerium/zirconium/rare earth metal mixed oxides in coating A are doped with lanthanum oxide.
11. Catalytic converter according to claim 1 , characterized in that
the lanthanum oxide content is >0% to 10% based on the weight of the respective cerium/zirconium/rare earth metal mixed oxide.
12. Catalytic converter according to claim 1 , characterized in that
the second cerium/zirconium/rare earth metal mixed oxide in coating A is doped not only with lanthanum oxide but also with a further metal oxide from the group of rare earth metal oxides.
13. Catalytic converter according to claim 12 , characterized in that
the second cerium/zirconium/rare earth metal mixed oxide in coating A is doped not only with lanthanum oxide but also with praseodymium.
14. Catalytic converter according to claim 1 , characterized in that
the cerium/zirconium/rare earth metal mixed oxide in coating B is doped with yttrium oxide and/or praseodymium oxide in addition to lanthanum oxide.
15. Catalytic converter according to claim 1 , characterized in that
the platinum group metal in layer A comprises at least one of platinum, palladium, or rhodium.
16. Catalytic converter according to claim 15 , characterized in that
the platinum group metal in layer B comprises at least one of platinum, palladium, or rhodium.
17. Catalytic converter according to claim 1 , characterized in that
the platinum group metal in layer B comprises at least one of platinum, palladium, or rhodium.
18. Method for removing carbon monoxide, hydrocarbons and nitrogen oxides out of the exhaust gas of combustion engines operated with stoichiometric air-fuel mixture,
characterized in that
the exhaust gas is conducted through a catalytic converter in accordance with claim 1 .