Method for producing press molded body
A method for producing a press molded body is provided in which a material X that contains a thermoplastic resin R x and carbon fibers A having a weight average fiber length L wA and a material Y that contains a thermoplastic resin R y and carbon fibers B having a weight average fiber length L wB are heated, and the heated material X and material Y are pressed within a mold at the same time, thereby producing a press molded body which has a region X that is formed of the material X and a region Y that is formed of the material Y. This method for producing a press molded body is configured such that: L wB <L wA ; L wB is from 0.1 mm to 15 mm (inclusive); and the press molded body has a transition zone XY where the region X and the region Y overlap with each other.
1. A method for producing a press molded body, comprising: heating X material having a pattern shape and containing carbon fibers A having a weight average fiber length LW A , and a thermoplastic resin R X ; heating Y material containing carbon fibers B having a weight average fiber length Lw B and a thermoplastic resin R Y , the Y material being prepared separately from the X material; and pressing the heated X material and the heated Y material simultaneously in a mold to produce the press molded body comprising an X region made of the X material and a Y region made of the Y material, wherein
Lw B <Lw A ,
Lw B is 0.1 mm or more and 15 mm or less, and
the press molded body further comprises a transition segment XY in which the X region and the Y region are laminated; and wherein at least one end portion of the press molded body in an in-plane direction consists of the Y region; and wherein the transition segment XY has a configuration in which the X region is sandwiched by the Y regions in a thickness direction, and the end portion in the in-plane direction consisting only of the Y region is continuously formed with the Y region of the transition segment XY.
2. The method for producing a press molded body according to claim 1 ,
wherein the Lw A is 1 mm or more.
3. The method for producing a press molded body according to claim 1 ,
wherein the Lw A is 1 mm or more and 100 mm or less.
4. The method for producing a press molded body according to claim 1 ,
wherein a carbon fiber volume fraction Vf x of the X material and a carbon fiber volume fraction Vf Y of the Y material satisfy a relationship of Vf x >Vf Y .
5. The method for producing a press molded body according to claim 1 ,
wherein the X material has a plate shape and the Y material flows and extends in an in-plane direction of the X material to produce the press molded body.
6. The method for producing a press molded body according to claim 1 ,
wherein a linear expansion coefficient E X in a plate thickness direction of a part consisting only of the X region, a linear expansion coefficient E XY in a plate thickness direction of the transition segment XY, and a linear expansion coefficient E Y in a plate thickness direction of a part consisting only of the Y region satisfy a relationship of E X >E XY >E Y .
7. The method for producing a press molded body according to claim 1 ,
wherein an extension rate D X of the X material is more than 0% and equal to or less than 50%, an extension rate D Y of the Y material is more than 10% and equal to or less than 60%, and D Y >D X .
8. The method for producing a press molded body according to claim 1 ,
wherein a ratio V x :V Y of a volume V x of the X material to a volume V Y of the Y material is 90:10 to 50:50.
9. The method for producing a press molded body according to claim 1 , wherein the Lw B is 5 mm or more and 15 mm or less.
10. The method for producing a press molded body according to claim 1 ,
wherein a shape of the X material is a shape developed by inverse molding analysis with a computer from a three-dimensional shape of the press molded body.
11. The method for producing a press molded body according to claim 1 ,
wherein the X material is cut off from a composite material containing carbon fibers and a thermoplastic resin.
12. The method for producing a press molded body according to claim 11 , wherein the Y material includes a material obtained by crushing scrap pieces remaining after the X material is cut off from the composite material.
13. The method for producing a press molded body according to claim 1 ,
wherein the press molded body has a flange portion, and at least one end portion of the flange portion is the Y region.
14. The method for producing a press molded body according to claim 1 ,
wherein the press molded body includes a part whose cross-sectional shape is a hat shape.
15. The method for producing a press molded body according to claim 14 ,
wherein the Y material was arranged on a mold surface in a region for forming a top panel having the hat shape and pressed.
16. The method for producing a press molded body according to claim 1 , further comprising:
cutting a raw material substrate containing the carbon fibers A and the thermoplastic resin RX into the X material having the pattern shape.