Compositions comprising multimodal ethylene-based polymers and low density polyethylene (LDPE)
Embodiments of polymer compositions and articles comprising such compositions containing at least one LDPE and at least one multimodal ethylene-based polymer having at least three ethylene-based components.
1. A polymer composition comprising:
at least one low density polyethylene (LDPE) having a density of 0.916 to 0.940 g/cc measured according to ASTM D792 and a melt index (I 2 ) from 0.1 to 10.0 g/10 min when measured according to ASTM D1238 at a load of 2.16 kg and temperature of 190° C.;
at least one multimodal ethylene-based polymer having a density from 0.900 to 0.940 g/cc and a melt index (I 2 ) from 0.1 to 10 g/10 min, the multimodal ethylene-based polymer comprising a first ethylene-based component, a second ethylene-based component, and a third ethylene-based component, wherein each of the first ethylene-based component, the second ethylene-based component, and the third ethylene-based component are polymerized reaction products of ethylene monomer and at least one C 3 -C 12 α-olefin comonomer, wherein:
the first ethylene-based component has a density of 0.870 to 0.915 g/cc, and a weight-average molecular weight (M w(GPC) ) from 163,000 g/mol to 363,000 g/mol as measured according to gel permeation chromatography (GPC), the multimodal ethylene-based polymer comprising at least 20% by weight of the first ethylene-based component;
the second ethylene-based component has a density greater than the density of the first ethylene-based component and less than 0.940 g/cc, and a weight-average molecular weight (M w(GPC) ) from 88,500 g/mol to 363,000 g/mol as measured according to GPC; and
the third ethylene-based component has a density greater than the density of the second ethylene-based component.
2. The polymer composition of claim 1 , wherein the first ethylene-based component and the second ethylene-based component each have a molecular weight distribution (MWD, M w(GPC) /M n(GPC) ) less than 3, where M w(GPC) is a weight average molecular weight and M n(GPC) is a number average molecular weight as measured by GPC, and wherein the first ethylene-based component has a C 3 -C 12 α-olefin comonomer incorporation of at least 0.5 mol%, and the second ethylene-based component has a C 3 -C 12 α-olefin comonomer incorporation of at least 0.5 mol%.
3. The polymer composition of claim 1 , wherein the multimodal ethylene-based polymer has a molecular weight distribution (M w(GPC) /M n(GPC) ) of at least 5.
4. The polymer composition of claim 1 , wherein the multimodal ethylene-based polymer comprises from 20 to 50% by weight of the first ethylene-based component, from 10 to 30% by weight of the second ethylene-based component, 25 to 60% by weight of the third ethylene-based component.
5. The polymer composition of claim 1 , wherein the melt index (I 2 ) of the multimodal ethylene-based polymer is from 0.1 to 5.0 g/10 min, where I 2 is measured according to ASTM D1238 at a load of 2.16 kg and temperature of 190° C.
6. The polymer composition of claim 1 , wherein the multimodal ethylene-based polymer has an I 10 /I 2 value from 9 to 15, where I 10 is measured according to ASTM D1238 at a load of 10 kg and temperature of 190° C.
7. The polymer composition of claim 1 , wherein the polymer composition comprises from 60 to 95% by weight of multimodal ethylene-based polymer and from 5 to 40% by weight of LDPE.
8. The polymer composition of claim 1 , wherein the LDPE has a molecular weight distribution (MWD) from 3.5 to 10 as measured by GPC.
9. The polymer composition of claim 1 , wherein the density of the first ethylene-based component is from 0.880 to 0.910 g/cc, and the melt index (I 2 ) of the first ethylene-based component is from 0.02 to 0.2 g/10 min.
10. The polymer composition of claim 1 , wherein the density of the second ethylene-based component is from 0.890 to 0.930 g/cc, and the melt index (I 2 ) of the second ethylene-based component is from 0.05 to 1.0 g/10 min.
11. The polymer composition of claim 1 , wherein the density of the third ethylene-based component is from 0.930 to 0.980 g/cc, and a weight-average molecular weight (M w(GPC) ) of less than 55,000 g/mol.
12. The polymer composition of claim 1 , wherein the C 3 -C 12 α-olefin comonomer is 1-octene or 1-hexene.
13. The polymer composition of claim 1 , wherein the third ethylene-based component has a melt index (I 2 ) greater than 50 g/10 mins.
14. The polymer composition of claim 1 , wherein the multimodal ethylene-based polymer has a crystallization elution fractionation (CEF) weight fraction greater than 23% and a weight-average molecular weight (M w(CEF) ) greater than 130,000 g/mol at a temperature range from 20° C. to T critical (T c ).
15. An article comprising the polymer composition of claim 1 , wherein the article is a blown film or a cast film.