Method for manufacturing disk-shaped glass blank and method for manufacturing glass substrate for magnetic disk
A glass blank is cut out from a glass plate by forming a crack starting portion inside the glass plate by moving a first laser beam relative to the glass plate such that a focal position of the laser beam is located in an inner portion of the glass plate in its thickness direction and the focal position forms a circle when viewed from a surface of the glass plate, then causing cracks to develop from the crack starting portion toward main surfaces of the glass plate, and splitting the glass plate to separate, from the glass plate, a glass blank that includes a separation surface having an arithmetic average surface roughness Ra smaller than 0.01 μm and a roundness not larger than 15 μm. Thereafter, main surfaces of the glass blank are ground or polished.
1. A method for manufacturing a disk-shaped glass blank, the method comprising:
separating a removal target portion from a glass plate to form a glass blank, the separating being performed by
forming a plurality of defects, which serve as core cracks, on a circular separation boundary line that is defined on a main surface of the glass plate such that a space is formed between adjacent defects of the plurality of defects, the forming of the plurality of defects being performed by emitting a first laser beam along the circular separation boundary line while moving the first laser beam relative to the glass plate, the first laser beam being a pulsed laser beam that has a pulse width not larger than 10 −12 seconds, and
forming a line-shaped defect by forming a crack connecting the plurality of defects; and
irradiating a separation surface of the glass blank with a second laser beam of a different type from the first laser beam from a direction of a normal to the separation surface, such that glass in a vicinity of the separation surface is heated and melted through the irradiating with the second laser beam, to form a chamfered surface on the separation surface, and to form the glass blank that has a roundness not larger than 15 μm and that has the separation surface having an arithmetic average surface roughness Ra smaller than 0.01 μm, the separation surface being a circumferential edge surface of the glass blank separated from the removal target portion, and the roundness indicating a difference between a radius of an inscribed circle and a radius of a circumscribed circle for a circumferential outline of the separation surface.
2. The method for manufacturing a disk-shaped glass blank according to claim 1 ,
wherein in the irradiating of the separation surface, the chamfered surface is formed such that the arithmetic average surface roughness Ra and the roundness of the glass blank are reduced, by irradiating an entire circumference of the separation surface from the direction of the normal to the separation surface with the second laser beam while the glass blank is rotated about a center position of the glass blank at a constant speed such that the second laser beam and the separation surface are moved relative to each other in a circumferential direction of the glass blank.
3. The method for manufacturing a disk-shaped glass blank according to claim 1 ,
wherein a thickness of the glass plate is not larger than 0.6 mm.
4. The method for manufacturing a disk-shaped glass blank according to claim 1 ,
wherein the roundness is 0.1 to 15 μm.
5. A method for manufacturing a glass substrate for a magnetic disk, the method comprising:
grinding/polishing processing in which at least one of grinding or polishing, or both is performed on the main surfaces of the glass blank obtained by the method for manufacturing a disk-shaped glass blank according to claim 1 .
6. The method for manufacturing a glass substrate for a magnetic disk according to claim 5 ,
wherein a thickness of the glass blank after the grinding/polishing processing is smaller than 0.52 mm.
7. The method for manufacturing a glass substrate for a magnetic disk according to claim 5 ,
wherein, in the grinding/polishing processing, the at least one of grinding or polishing, or both is performed on the main surfaces of the glass blank while maintaining the roundness of the glass blank and the arithmetic average surface roughness of at least a portion of the separation surface.